PPA LNP™ THERMOCOMP™ UF-1007 BK SABIC INNOVATIVE US
124
- Unit Price:
- $3024 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 23.3MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Filler: Glass fiber reinf High temperature resistan
- Application Areas:Automotive components
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD | ISO294-4 | 0.15 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 11.0 | kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO180/1U | 45.0 | kJ/m² |
| elongation at break | 5mm/min，23°C | ISO527-2 | 2.0 | % |
| Tensile modulus | 1mm/min，23°C | ISO527-2 | 12100 | Mpa |
| tensile strength | 5mm/min，23°C | ISO527-2 | 194 | Mpa |
| Bending modulus | 2mm/min，23°C | ISO178 | 9600 | Mpa |
| bending strength | Yield，2mm/min，23°C | ISO178 | 279 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.80MPaAnnealed | ISO75-2/Af | 269 | °C |
| Coefficient of linear expansion | TD | ISO11359-2 | 5.9E-05 | cm/cm/°C |
| MD | ISO11359-2 | 2.2E-05 | cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.