Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPA UF-1007 BK SABIC INNOVATIVE US
LNP™ THERMOCOMP™
Automotive components
Filler: Glass fiber reinf、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPA/SABIC INNOVATIVE US/UF-1007 BK
Shrinkage rate
MD
ISO294-4
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPA/SABIC INNOVATIVE US/UF-1007 BK
elongation at break
5mm/min，23°C
ISO527-2
%
2
Tensile modulus
1mm/min，23°C
ISO527-2
Mpa
1
tensile strength
5mm/min，23°C
ISO527-2
Mpa
1
Bending modulus
2mm/min，23°C
ISO178
Mpa
9
bending strength
屈服，2mm/min，23°C
ISO178
Mpa
2
Impact strength of cantilever beam gap
23°C
ISO180/1A
kJ/m²
1
Suspended wall beam without notch impact strength
23°C
ISO180/1U
kJ/m²
4
Thermal performance
Test Condition
Test Method
Unit
PPA/SABIC INNOVATIVE US/UF-1007 BK
Hot deformation temperature
1.80MPa退火
ISO75-2/Af
°C
2
Coefficient of linear expansion
MD
ISO11359-2
cm/cm/°C
2
Coefficient of linear expansion
TD
ISO11359-2
cm/cm/°C
5