ASA GELOY™ CR3020 BL4A291 SABIC INNOVATIVE US
107
- Unit Price:
- $2346 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 31MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low gloss Low glossiness
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTMD792 | 1.07 | g/cm³ | |
| ISO1183 | 1.07 | g/cm³ | ||
| Melt mass flow rate | 220°C/10.0kg | ASTMD1238 | 5.0 | g/10min |
| 220°C/10.0kg | ISO1133 | 6.4 | g/10min | |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.55to0.63 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending modulus | 50.0mm跨距 | ASTMD790 | 1860 | Mpa |
| ISO178 | 1800 | Mpa | ||
| Tensile strength | 断裂 | ASTMD638 | 30.0 | Mpa |
| Tensile stress | 断裂 | ISO527-2/50 | 31.0 | Mpa |
| elongation | 屈服 | ASTMD638 | 3.5 | % |
| Tensile strain | 屈服 | ISO527-2/50 | 3.4 | % |
| elongation | 断裂 | ASTMD638 | 38 | % |
| Tensile strain | 断裂 | ISO527-2/50 | 23 | % |
| bending strength | 屈服,50.0mm跨距 | ASTMD790 | 57.0 | Mpa |
| Tensile stress | 屈服 | ISO527-2/50 | 39.0 | Mpa |
| bending strength | ISO178 | 56.0 | Mpa | |
| Tensile modulus | ASTMD638 | 1840 | Mpa | |
| ISO527-2/1 | 1800 | Mpa | ||
| Tensile strength | 屈服 | ASTMD638 | 39.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | MD：-40到40°C | ISO11359-2 | 1.4E-04 | cm/cm/°C |
| TD：-40到40°C | ISO11359-2 | 2E-04 | cm/cm/°C | |
| Hot deformation temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 74.0 | °C |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 77.0 | °C | |
| Vicat softening temperature | ASTMD15259 | 100 | °C | |
| ISO306/B50 | 100 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ASTMD256 | 1.2 | J/m |
| 23°C | ASTMD256 | 8.4 | J/m | |
| -30°C | ISO180/1A | 3.8 | kJ/m² | |
| 23°C | ISO180/1A | 26 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 4.50 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.