Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ASA CR3020 BL4A291 SABIC INNOVATIVE US
GELOY™
--
Low gloss、Low glossiness
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
ASA/SABIC INNOVATIVE US/CR3020 BL4A291
density
ASTMD792
g/cm³
1
density
ISO1183
g/cm³
1
Melt mass flow rate
220°C/10.0kg
ASTMD1238
g/10min
5
Melt mass flow rate
220°C/10.0kg
ISO1133
g/10min
6
Shrinkage rate
MD：3.20mm
内部方法
%
0
Mechanical performance
Test Condition
Test Method
Unit
ASA/SABIC INNOVATIVE US/CR3020 BL4A291
Tensile strength
屈服
ASTMD638
Mpa
3
Tensile strength
断裂
ASTMD638
Mpa
3
Tensile modulus
ASTMD638
Mpa
1
Tensile modulus
ISO527-2/1
Mpa
1
Tensile strain
屈服
ISO527-2/50
%
3
Tensile strain
断裂
ISO527-2/50
%
2
Tensile stress
断裂
ISO527-2/50
Mpa
3
Tensile stress
屈服
ISO527-2/50
Mpa
3
elongation
屈服
ASTMD638
%
3
elongation
断裂
ASTMD638
%
3
Bending modulus
50.0mm跨距
ASTMD790
Mpa
1
Bending modulus
ISO178
Mpa
1
bending strength
屈服,50.0mm跨距
ASTMD790
Mpa
5
bending strength
ISO178
Mpa
5
Thermal performance
Test Condition
Test Method
Unit
ASA/SABIC INNOVATIVE US/CR3020 BL4A291
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
7
Hot deformation temperature
1.8MPa,Unannealed,64.0mmSpan
ISO75-2/Af
°C
7
Vicat softening temperature
ASTMD15259
°C
1
Vicat softening temperature
ISO306/B50
°C
1
Linear coefficient of thermal expansion
MD：-40到40°C
ISO11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
TD：-40到40°C
ISO11359-2
cm/cm/°C
2
Impact performance
Test Condition
Test Method
Unit
ASA/SABIC INNOVATIVE US/CR3020 BL4A291
Impact strength of cantilever beam gap
-30°C
ASTMD256
J/m
1
Impact strength of cantilever beam gap
23°C
ASTMD256
J/m
8
Impact strength of cantilever beam gap
-30°C
ISO180/1A
kJ/m²
3
Impact strength of cantilever beam gap
23°C
ISO180/1A
kJ/m²
2
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
4