ASA Luran®S 776SE BASF GERMANY
132
- Unit Price:
- $2173 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Good strength
- Application Areas:--
- Color:--
- Grade:Heat resistant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | ISO294-4 | 0.50to0.90 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 1.7 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.35 | % | |
| Melt volume flow rate | 220°C/10.0kg | ISO1133 | 4.00 | cm3/10min |
| Density/specific gravity | ISO1183 | 1.07 | g/cm³ | |
| Apparent density 2 | 0.59 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending stress | ISO178 | 65.0 | Mpa | |
| TensileCreepModule | 1hr | ISO899-1 | 2000 | Mpa |
| Tensile stress | Yield,23°C | ISO527-2 | 47.0 | Mpa |
| Tensile strain | Yield,23°C | ISO527-2 | 3.3 | % |
| Tensile creep modulus | 1000hr | ISO899-1 | 1200 | Mpa |
| Tensile modulus | ISO527-2 | 2200 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat softening temperature | -- | ISO306/A50 | 104 | °C |
| -- | ISO306/B50 | 92.0 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 8.0E-5to1.1E-4 | cm/cm/°C |
| thermal conductivity | DIN52612 | 0.17 | W/m/K | |
| Hot deformation temperature 3 | 0.45MPa,Annealed | ISO75-2/B | 101 | °C |
| 1.8MPa,Annealed | ISO75-2/A | 96.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 1E+13 | ohms | |
| Dielectric constant | 100Hz | IEC60250 | 3.80 | |
| Volume resistivity | IEC60093 | 1E+14 | ohms·cm | |
| Dissipation factor | 100Hz | IEC60250 | 9E-03 | |
| 1MHz | IEC60250 | 0.034 |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Elongation MD | Break | ISO527-3 | 12 | % |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179 | 4.0 | kJ/m² |
| 23°C | ISO179 | 30 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO180/A | 4.0 | kJ/m² |
| 23°C | ISO180/A | 15 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | ISO2039-1 | 70.0 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.