Density/specific gravity

ISO1183

g/cm³

1

Melt volume flow rate

220°C/10.0kg

ISO1133

cm3/10min

4

Shrinkage rate

ISO294-4

%

0

Water absorption rate

饱和,23°C

ISO62

%

1

Water absorption rate

平衡,23°C,50%RH

ISO62

%

0

TensileCreepModule

1hr

ISO899-1

Mpa

2

Tensile modulus

ISO527-2

Mpa

2

Tensile creep modulus

1000hr

ISO899-1

Mpa

1

Tensile strain

屈服,23°C

ISO527-2

%

3

Tensile stress

屈服,23°C

ISO527-2

Mpa

4

Bending stress

ISO178

Mpa

6

thermal conductivity

DIN52612

W/m/K

0

Hot deformation temperature 3

0.45MPa,Annealed

ISO75-2/B

°C

1

Hot deformation temperature 3

1.8MPa,Annealed

ISO75-2/A

°C

9

Vicat softening temperature

--

ISO306/A50

°C

1

Vicat softening temperature

--

ISO306/B50

°C

9

Linear coefficient of thermal expansion

MD

ISO11359-2

cm/cm/°C

8

Surface resistivity

IEC60093

ohms

1

Volume resistivity

IEC60093

ohms·cm

1

Elongation MD

断裂

ISO527-3

%

1

Charpy Notched Impact Strength

-30°C

ISO179

kJ/m²

4

Charpy Notched Impact Strength

23°C

ISO179

kJ/m²

3

Impact strength of cantilever beam gap

-30°C

ISO180/A

kJ/m²

4

Impact strength of cantilever beam gap

23°C

ISO180/A

kJ/m²

1

Ball pressure hardness

ISO2039-1

Mpa

7