MVLDPE DOWLEX™ 2045.11G STYRON US
126
- Unit Price:
- $1445 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 190°C/2.16kg | ASTMD1238 | 1.0 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tangent modulus (MD) | 20.3um | ASTM D-882 | 227 | Mpa |
| Tangent modulus (TD) | 20.3um | ASTM D-882 | 247 | Mpa |
| Tangent modulus (MD) | 2% Secant，50.8um | ASTM D-882 | 196 | Mpa |
| Tangent modulus (TD) | 2% Secant，50.8um | ASTM D-882 | 234 | Mpa |
| Tensile yield strength (TD) | 20.3um | ASTM D-882 | 13.1 | Mpa |
| Tensile yield strength (MD) | 20.3um | ASTM D-882 | 12.7 | Mpa |
| 50.8um | ASTM D-882 | 11.8 | Mpa | |
| Tensile yield strength (TD) | 50.8um | ASTM D-882 | 12.6 | Mpa |
| Tensile strength at break (MD) | 20.3um | ASTM D-882 | 60.4 | Mpa |
| Tensile fracture strength (TD) | 20.3um | ASTM D-882 | 49.2 | Mpa |
| Tensile strength at break (MD) | 50.8um | ASTM D-882 | 51.9 | Mpa |
| Tensile fracture strength (TD) | 50.8um | ASTM D-882 | 44.3 | Mpa |
| Tensile elongation at break (MD) | 20.3um | ASTM D-882 | 480 | % |
| Tensile elongation at break (TD) | 20.3um | ASTM D-882 | 750 | % |
| 50.8um | ASTM D-882 | 770 | % | |
| Tensile elongation at break (MD) | 50.8um | ASTM D-882 | 670 | % |
| Falling hammer impact | 20.3um | ASTM D-1709A | 130 | g |
| 50.8um | ASTM D-1709A | 280 | g | |
| Elmendorf Tear Strength (TD) | 20.3um | ASTM D-1922 | 580 | g |
| Elmendorf Tear Strength (MD) | 20.3um | ASTM D-1922 | 440 | g |
| Elmendorf Tear Strength (TD) | 50.8um | ASTM D-1922 | 1200 | g |
| Elmendorf Tear Strength (MD) | 50.8um | ASTM D-1922 | 740 | g |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | ASTM D-1525 | 104 | °C | |
| Melting temperature | Internal Method | 122 | °C | |
| Vicat softening temperature | ASTMD1525 | 104 | °C | |
| Melting temperature (DSC) | 内部方法 | 122 | °C |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Film thickness - tested | 内部方法 | 25 | µm | |
| Membrane puncture strength | 内部方法 | 1.24 | J | |
| Membrane piercing force | 内部方法 | 31.1 | N | |
| Membrane puncture resistance | 内部方法 | 6.21 | J/cm³ | |
| Membrane strength | MD | ASTMD882 | 110 | J/cm³ |
| TD | ASTMD882 | 114 | J/cm³ | |
| Secant modulus | 1%Secant,MD | ASTMD882 | 211 | Mpa |
| 2%Secant,MD | ASTMD882 | 172 | Mpa | |
| 1%Secant,TD | ASTMD882 | 234 | Mpa | |
| 2%Secant,TD | ASTMD882 | 189 | Mpa | |
| Tensile strength | MD:Yield | ASTMD882 | 13.4 | Mpa |
| TD:Yield | ASTMD882 | 14.1 | Mpa | |
| MD:Break | ASTMD882 | 46.1 | Mpa | |
| TD:Break | ASTMD882 | 35.3 | Mpa | |
| elongation | MD:Break | ASTMD882 | 540 | % |
| TD:Break | ASTMD882 | 660 | % | |
| Falling hammer impact | ASTMD1709A | 180 | g | |
| Elmondov tear strength | MD | ASTMD1922 | 440 | g |
| TD | ASTMD1922 | 630 | g |
| Processing performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Temperature | 221-232 | °C |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Film Resilience (TD) | 20.3um | ASTM D-882 | 304 | J/cm³ |
| Film Resilience (MD) | 20.3um | ASTM D-882 | 240 | J/cm4 |
| 50.8um | ASTM D-882 | 273 | J/cm5 | |
| Film Resilience (TD) | 50.8um | ASTM D-882 | 292 | J/cm6 |
| Film puncture resistance | 20.3um | Internal Method | 11.4 | J/cm³ |
| 50.8um | Internal Method | 9.76 | J/cm³ |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| gloss | 45° | ASTMD2457 | 34 | |
| Haze | ASTMD1003 | 20 | % | |
| gloss | 45°，20.3um | ASTM D-2457 | 70 | |
| 45°，50.8um | ASTM D-2457 | 67 | ||
| Haze | 20.3um | ASTM D-1003 | 7 | % |
| 50.8um | ASTM D-1003 | 10 | % |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D-792 | 0.922 | g/m3 | |
| Melt flow rate | 190℃/2.16kg | ASTM D-1238 | 1 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.