Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
MVLDPE 2045.11G STYRON US
DOWLEX™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
MVLDPE/STYRON US/2045.11G
Melt mass flow rate
190°C/2.16kg
ASTMD1238
g/10min
1
Mechanical performance
Test Condition
Test Method
Unit
MVLDPE/STYRON US/2045.11G
Elmendorf Tear Strength (MD)
20.3um
ASTM D-1922
g
4
Elmendorf Tear Strength (MD)
50.8um
ASTM D-1922
g
7
Elmendorf Tear Strength (TD)
50.8um
ASTM D-1922
g
1
Elmendorf Tear Strength (TD)
20.3um
ASTM D-1922
g
5
Tangent modulus (MD)
20.3um
ASTM D-882
Mpa
2
Tangent modulus (MD)
2% Secant，50.8um
ASTM D-882
Mpa
1
Tangent modulus (TD)
2% Secant，50.8um
ASTM D-882
Mpa
2
Tangent modulus (TD)
20.3um
ASTM D-882
Mpa
2
Tensile strength at break (MD)
50.8um
ASTM D-882
Mpa
5
Tensile strength at break (MD)
20.3um
ASTM D-882
Mpa
6
Tensile fracture strength (TD)
20.3um
ASTM D-882
Mpa
4
Tensile fracture strength (TD)
50.8um
ASTM D-882
Mpa
4
Tensile elongation at break (MD)
20.3um
ASTM D-882
%
4
Tensile elongation at break (MD)
50.8um
ASTM D-882
%
6
Tensile elongation at break (TD)
20.3um
ASTM D-882
%
7
Tensile elongation at break (TD)
50.8um
ASTM D-882
%
7
Tensile yield strength (MD)
20.3um
ASTM D-882
Mpa
1
Tensile yield strength (MD)
50.8um
ASTM D-882
Mpa
1
Tensile yield strength (TD)
50.8um
ASTM D-882
Mpa
1
Tensile yield strength (TD)
20.3um
ASTM D-882
Mpa
1
Falling hammer impact
20.3um
ASTM D-1709A
g
1
Falling hammer impact
50.8um
ASTM D-1709A
g
2
Thermal performance
Test Condition
Test Method
Unit
MVLDPE/STYRON US/2045.11G
Melting temperature (DSC)
内部方法
°C
1
Melting temperature
Internal Method
°C
1
vicat softening point
ASTM D-1525
°C
1
Vicat softening temperature
ASTMD1525
°C
1
film
Test Condition
Test Method
Unit
MVLDPE/STYRON US/2045.11G
Elmondov tear strength
MD
ASTMD1922
g
4
Elmondov tear strength
TD
ASTMD1922
g
6
Film thickness - tested
内部方法
µm
2
Secant modulus
1%正割,MD
ASTMD882
Mpa
2
Secant modulus
2%正割,MD
ASTMD882
Mpa
1
Secant modulus
1%正割,TD
ASTMD882
Mpa
2
Secant modulus
2%正割,TD
ASTMD882
Mpa
1
Tensile strength
MD:屈服
ASTMD882
Mpa
1
Tensile strength
TD:屈服
ASTMD882
Mpa
1
Tensile strength
MD:断裂
ASTMD882
Mpa
4
Tensile strength
TD:断裂
ASTMD882
Mpa
3
Falling hammer impact
ASTMD1709A
g
1
Membrane piercing force
内部方法
N
3
Membrane puncture strength
内部方法
J
1
Membrane puncture resistance
内部方法
J/cm³
6
Membrane strength
MD
ASTMD882
J/cm³
1
Membrane strength
TD
ASTMD882
J/cm³
1
elongation
MD:断裂
ASTMD882
%
5
elongation
TD:断裂
ASTMD882
%
6
Other performance
Test Condition
Test Method
Unit
MVLDPE/STYRON US/2045.11G
Film puncture resistance
20.3um
Internal Method
J/cm³
1
Film puncture resistance
50.8um
Internal Method
J/cm³
9
Film Resilience (MD)
20.3um
ASTM D-882
J/cm4
2
Film Resilience (MD)
50.8um
ASTM D-882
J/cm5
2
Film Resilience (TD)
50.8um
ASTM D-882
J/cm6
2
Film Resilience (TD)
20.3um
ASTM D-882
J/cm³
3
optical performance
Test Condition
Test Method
Unit
MVLDPE/STYRON US/2045.11G
Haze
ASTMD1003
%
2
Haze
20.3um
ASTM D-1003
%
7
Haze
50.8um
ASTM D-1003
%
1
Basic performance
Test Condition
Test Method
Unit
MVLDPE/STYRON US/2045.11G
density
ASTM D-792
g/m3
0
Melt flow rate
190℃/2.16kg
ASTM D-1238
g/10min
1