PEI EXTEM™ VH1003-1000 SABIC INNOVATIVE US

126

Unit Price:
$20416 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Chemical resistance heat-resisting Flame retardant high strength
Application Areas:aviation industry Automotive sector
Color:--
Grade:--

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	MD1	内部方法	0.50到0.70	%
	Shrinkage rate	MD:3.20mm	内部方法	0.50到0.70	%
	Shrinkage rate	Shrinkage rate	TD:3.20mm	内部方法	0.50到0.70	%
Water absorption rate	Saturation,23°C	ISO62	1.8	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO62	0.60	%
Melt mass flow rate	367°C/6.6kg	ASTMD1238	16	g/10min
Melt volume flow rate	360°C/5.0kg	ISO1133	8.50	cm3/10min

Mechanical performance	Test Condition	Test Method	Test Result	Unit
--9		ISO178	123	Mpa
--8		ISO178	3080	Mpa
yield		ISO527-2/5	95.0	Mpa
yield	yield		ISO527-2/5	8.5	%
crack		ISO527-2/5	78.0	Mpa
crack	crack		ISO527-2/5	17	%
--2		ASTMD638	3520	Mpa
Surrender 3		ASTMD638	96.5	Mpa
Fracture 6		ASTMD638	50	%
50.0mm span 7		ASTMD790	3170	Mpa
Fracture 4		ASTMD638	96.5	Mpa
Surrender 5		ASTMD638	6.0	%
Fracture, 50.0mm span 11		ASTMD790	159	Mpa
Yield, 100mm span of 10		ASTMD790	155	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
1.8MPa, unannealed, 3.20mm		ASTMD648	217	°C
Flow: -40 to 150 ° C		ASTME831	5E-05	cm/cm/°C
Flow: 23 to 150 ° C		ISO11359-2	5E-05	cm/cm/°C
Horizontal: -40 to 150 ° C		ASTME831	5E-05	cm/cm/°C
Horizontal: 23 to 150 ° C		ISO11359-2	5E-05	cm/cm/°C
1.8MPa, unannealed, 64.0mm span 16		ISO75-2/Af	228	°C
BallPressure Test	125°C	IEC60695-10-2	Pass
1.8MPa, unannealed, 6.40mm		ASTMD648	230	°C
0.45MPa, unannealed, 6.40mm		ASTMD648	237	°C
thermal conductivity		ASTME1530	0.22	W/m/K
--		ASTMD1525,ISO306/B501217	242	°C
--	--		ISO306/B120	238	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Leakage Trace Index		IEC60112	175	V
Dielectric constant	100Hz	ASTMD150	3.41
Dielectric constant	Dielectric constant	1kHz	ASTMD150	3.41
Dissipation factor	100Hz	IEC60250	8E-03
	Dissipation factor	1kHz	IEC60250	1E-03
		Dissipation factor	1MHz	IEC60250	7E-03
			Dissipation factor	50Hz	IEC60250	0.025
			Dissipation factor	Dissipation factor	60Hz	IEC60250	0.025
Dielectric strength	3.20mm,inOil	ASTMD149	17	KV/mm

Impact performance	Test Condition	Test Method	Test Result	Unit
Dart impact equipped with measuring instruments	23°C,TotalEnergy	ASTMD3763	33.9	J
23°C		ASTMD256	69	J/m
23°C	23°C		ASTMD4812,ISO180/1U	无断裂
-30°C		ASTMD256	74	J/m
-30°C15		ISO180/1U	无断裂
-30°C13		ISO180/1A	5.4	kJ/m²
23°C14		ISO180/1A	4.6	kJ/m²
The impact strength of a simply supported beam without a notch is 12	-30°C	ISO179/1eU	无断裂
	The impact strength of a simply supported beam without a notch is 12	23°C	ISO179/1eU	无断裂

hardness	Test Condition	Test Method	Test Result	Unit
Ball pressure hardness	H358/30	ISO2039-1	141	Mpa

optical performance	Test Condition	Test Method	Test Result	Unit
Haze	2540µm	ASTMD1003	2.0	%
transmissivity	2540µm	ASTMD1003	58.0	%

flammability	Test Condition	Test Method	Test Result	Unit
Burning wire flammability index	3.20mm	IEC60695-2-12	960	°C
Extreme Oxygen Index		ISO4589-2	45	%
Hot filament ignition temperature	3.00mm	IEC60695-2-13	850	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.