Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI VH1003-1000 SABIC INNOVATIVE US
EXTEM™
aviation industry、Automotive sector
Chemical resistance、heat-resisting、Flame retardant、high strength
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/VH1003-1000
Melt volume flow rate
360°C/5.0kg
ISO1133
cm3/10min
8
Melt mass flow rate
367°C/6.6kg
ASTMD1238
g/10min
1
Shrinkage rate
MD1
内部方法
%
0
Shrinkage rate
MD:3.20mm
内部方法
%
0
Shrinkage rate
TD:3.20mm
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
1
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/VH1003-1000
--
ISO527-2/1
Mpa
3
--2
ASTMD638
Mpa
3
50.0mm span 7
ASTMD790
Mpa
3
--8
ISO178
Mpa
3
--9
ISO178
Mpa
1
crack
ISO527-2/5
Mpa
7
crack
ISO527-2/5
%
1
Fracture, 50.0mm span 11
ASTMD790
Mpa
1
Fracture 4
ASTMD638
Mpa
9
Fracture 6
ASTMD638
%
5
yield
ISO527-2/5
%
8
yield
ISO527-2/5
Mpa
9
Yield, 100mm span of 10
ASTMD790
Mpa
1
Surrender 3
ASTMD638
Mpa
9
Surrender 5
ASTMD638
%
6
Thermal performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/VH1003-1000
--
ASTMD1525,ISO306/B501217
°C
2
--
ISO306/B120
°C
2
0.45MPa, unannealed, 6.40mm
ASTMD648
°C
2
1.8MPa, unannealed, 3.20mm
ASTMD648
°C
2
1.8MPa, unannealed, 6.40mm
ASTMD648
°C
2
1.8MPa, unannealed, 64.0mm span 16
ISO75-2/Af
°C
2
thermal conductivity
ASTME1530
W/m/K
0
Horizontal: 23 to 150 ° C
ISO11359-2
cm/cm/°C
5
Horizontal: -40 to 150 ° C
ASTME831
cm/cm/°C
5
Flow: 23 to 150 ° C
ISO11359-2
cm/cm/°C
5
Flow: -40 to 150 ° C
ASTME831
cm/cm/°C
5
Electrical performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/VH1003-1000
Dielectric strength
3.20mm,inOil
ASTMD149
KV/mm
1
Leakage Trace Index
IEC60112
V
1
Impact performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/VH1003-1000
23°C
ASTMD256
J/m
6
23°C14
ISO180/1A
kJ/m²
4
-30°C
ASTMD256
J/m
7
-30°C13
ISO180/1A
kJ/m²
5
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
3
hardness
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/VH1003-1000
Ball pressure hardness
H358/30
ISO2039-1
Mpa
1
flammability
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/VH1003-1000
Extreme Oxygen Index
ISO4589-2
%
4
Hot filament ignition temperature
3.00mm
IEC60695-2-13
°C
8
Burning wire flammability index
3.20mm
IEC60695-2-12
°C
9
optical performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/VH1003-1000
transmissivity
2540µm
ASTMD1003
%
5
Haze
2540µm
ASTMD1003
%
2