PEI ULTEM™ 9085-1100 SABIC INNOVATIVE US
109
- Unit Price:
- $42947 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility Low toxicity Low smoke
- Application Areas:Aircraft interior parts national defense Railway Applications Profile
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| Water absorption rate | Saturation,23°C | ISO62 | 0.39 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.17 | % | |
| Melt mass flow rate | 295°C/6.6kg | ASTMD1238 | 8.9 | g/10min |
| Melt volume flow rate | 360°C/5.0kg | ISO1133 | 65.5 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strain | Yield | ISO527-2/5 | 6.7 | % |
| Elongation rate 4 | Break | ASTMD638 | 72 | % |
| Tensile strain | Break | ISO527-2/5 | 50 | % |
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 2920 | Mpa |
| Bending modulus 5 | ISO178 | 2750 | Mpa | |
| Bending strength 5,6 | ISO178 | 90.0 | Mpa | |
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 138 | Mpa |
| Tensile modulus 2 | ASTMD638 | 3440 | Mpa | |
| Tensile modulus | ISO527-2/1 | 3050 | Mpa | |
| Tensile strength 3 | Yield | ASTMD638 | 84.0 | Mpa |
| Tensile stress | Yield | ISO527-2/5 | 88.0 | Mpa |
| Tensile strength 3 | Break | ASTMD638 | 74.0 | Mpa |
| Tensile stress | Break | ISO527-2/5 | 71.0 | Mpa |
| Elongation rate 3 | Yield | ASTMD638 | 7.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature 8 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 152 | °C |
| Vicat softening temperature | ISO306/B120 | 173 | °C | |
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 153 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| NotchedIzodImpactStrength7 | 23°C | ISO180/1A | 13 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Extreme Oxygen Index | ASTMD2863 | 49 | % | |
| FAAFlammability9 | FAR25.853 | <5 | ||
| OSU peak heat release rate 10 | FAR25.853 | 36.0 | kW/m² | |
| OSU total heat release 11 | FAR25.853 | 16.0 | kW·min/m² | |
| VerticalBurnTest | 60s),passesat | FAR25.853 | 2.0 | sec |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.