PEI 9085-1100 SABIC INNOVATIVE US
ULTEM™
Aircraft interior parts、national defense、Railway Applications、Profile
High mobility、Low toxicity、Low smoke
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/9085-1100
Melt volume flow rate
360°C/5.0kg
ISO1133
cm3/10min
6
Melt mass flow rate
295°C/6.6kg
ASTMD1238
g/10min
8
Shrinkage rate
MD：3.20mm
内部方法
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/9085-1100
Tensile strength 3
断裂
ASTMD638
Mpa
7
Tensile strength 3
屈服
ASTMD638
Mpa
8
Tensile modulus
ISO527-2/1
Mpa
3
Tensile modulus 2
ASTMD638
Mpa
3
Tensile strain
断裂
ISO527-2/5
%
5
Tensile strain
屈服
ISO527-2/5
%
6
Tensile stress
断裂
ISO527-2/5
Mpa
7
Tensile stress
屈服
ISO527-2/5
Mpa
8
Elongation rate 3
屈服
ASTMD638
%
7
Elongation rate 4
断裂
ASTMD638
%
7
Bending modulus 4
50.0mm跨距
ASTMD790
Mpa
2
Bending modulus 5
ISO178
Mpa
2
Bending strength 4
屈服,50.0mm跨距
ASTMD790
Mpa
1
Bending strength 5,6
ISO178
Mpa
9
Thermal performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/9085-1100
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature 8
1.8MPa,Unannealed,64.0mmSpan
ISO75-2/Af
°C
1
Vicat softening temperature
ISO306/B120
°C
1
Impact performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/9085-1100
NotchedIzodImpactStrength7
23°C
ISO180/1A
kJ/m²
1
flammability
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/9085-1100
OSU peak heat release rate 10
FAR25.853
kW/m²
3
OSU total heat release 11
FAR25.853
kW·min/m²
1
VerticalBurnTest
60s),passesat
FAR25.853
sec
2
Extreme Oxygen Index
ASTMD2863
%
4