PEI ULTEM™ HU1000-1H1000 SABIC INNOVATIVE US
134
- Unit Price:
- $24503 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Middle flow Biocompatibility Steam sterilization
- Application Areas:Medical and nursing suppl Medical devices
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt flow rate | 337°C/6.6 kg | ASTM D1238 | 9.0 | g/10 min |
| Molten Volume Flow Rate (MVR) | 220°C/5.0 kg | ISO 1133 | 13.0 | cm3/10min |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
| Water absorption rate | 24 hr | ASTM D570 | 0.25 | % |
| Saturation, 23°C | ISO 62 | 1.3 | % | |
| Equilibrium, 23°C | ASTM D570 | 1.3 | % | |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | -- 2 | ASTM D638 | 3580 | Mpa |
| -- | ISO 527-2/1 | 3200 | Mpa | |
| Tensile strength | Yield 3 | ASTM D638 | 110 | Mpa |
| Yield | ISO 527-2/5 | 105 | Mpa | |
| Break 3 | ASTM D638 | 90.0 | Mpa | |
| Break | ISO 527-2/5 | 85.0 | Mpa | |
| elongation | Yield 3 | ASTM D638 | 7.0 | % |
| Yield | ISO 527-2/5 | 6.0 | % | |
| Break 3 | ASTM D638 | 60 | % | |
| Break | ISO 527-2/5 | 60 | % | |
| Bending modulus | 50.0 mm Span 4 | ASTM D790 | 3430 | Mpa |
| -- 5 | ISO 178 | 3300 | Mpa | |
| Bending stress | -- 5, 6 | ISO 178 | 160 | Mpa |
| Yield, 50.0 mm Span 4 | ASTM D790 | 173 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Thermal deformation temperature under load | 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 201 | °C |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 8 | ISO 75-2/Af | 215 | °C | |
| Vicat softening temperature | -- | ASTM D15259 | 218 | °C |
| -- | ISO 306/B50 | 215 | °C | |
| -- | ISO 306/B120 | 211 | °C | |
| Linear coefficient of thermal expansion | Flow : -20 to 150°C | ASTM E831 | 5.6E-5 | cm/cm/°C |
| Flow : -40 to 40°C | ISO 11359-2 | 5.0E-5 | cm/cm/°C | |
| Across Flow : -20 to 150°C | ASTM E831 | 5.4E-5 | cm/cm/°C | |
| Across Flow : -40°C | ISO 11359-2 | 5.0E-5 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | ASTM D257 | 1.0E+17 | ohms·cm | |
| Dielectric strength | 1.60 mm, in Air | ASTM D149 | 33 | KV/mm |
| 1.60 mm, in Oil | ASTM D149 | 28 | KV/mm | |
| Dielectric constant | 1 kHz | ASTM D150 | 3.15 | |
| Dissipation factor | 1 kHz | ASTM D150 | 1.3E-3 | |
| 2.45 GHz | ASTM D150 | 2.5E-3 | ||
| Arc resistance 10 | ASTM D495 | PLC 5 | ||
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 4 | ||
| High arc combustion index (HAI) 11 | UL 746 | PLC 3 | ||
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 2 | ||
| Hot wire ignition (HWI) | UL 746 | PLC 1 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 150 | °C | ||
| drying time | 4.0 到 6.0 | hr | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Suggested injection volume | 40 到 60 | % | ||
| Temperature at the rear of the barrel | 330 到 400 | °C | ||
| Temperature in the middle of the barrel | 340 到 400 | °C | ||
| Temperature at the front of the material cylinder | 345 到 400 | °C | ||
| Spray nozzle temperature | 345 到 400 | °C | ||
| Processing (melt) temperature | 350 到 400 | °C | ||
| Mold temperature | 135 到 165 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 40 到 70 | rpm | ||
| Exhaust hole depth | 0.025 到 0.076 | mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Non notched cantilever beam impact | 23°C | ASTM D4812 | 1300 | J/m |
| Dart impact equipped with measuring instruments | 23°C, Total Energy | ASTM D3763 | 0.00 | J |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Extreme Oxygen Index | ASTM D2863 | 47 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.