Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI HU1000-1H1000 SABIC INNOVATIVE US
ULTEM™
Medical and nursing suppl、Medical devices
Middle flow、Biocompatibility、Steam sterilization
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/HU1000-1H1000
Melt flow rate
337°C/6.6 kg
ASTM D1238
g/10 min
9
Molten Volume Flow Rate (MVR)
220°C/5.0 kg
ISO 1133
cm3/10min
1
Shrinkage rate - flow
3.20 mm
内部方法
%
0
Water absorption rate
平衡, 23°C, 50% RH
ISO 62
%
0
Water absorption rate
平衡, 23°C
ASTM D570
%
1
Water absorption rate
饱和, 23°C
ISO 62
%
1
Water absorption rate
24 hr
ASTM D570
%
0
Mechanical performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/HU1000-1H1000
Tensile strength
断裂
ISO 527-2/5
Mpa
8
Tensile strength
断裂 3
ASTM D638
Mpa
9
Tensile strength
屈服
ISO 527-2/5
Mpa
1
Tensile strength
屈服 3
ASTM D638
Mpa
1
Tensile modulus
--
ISO 527-2/1
Mpa
3
Tensile modulus
-- 2
ASTM D638
Mpa
3
elongation
断裂
ISO 527-2/5
%
6
elongation
断裂 3
ASTM D638
%
6
elongation
屈服
ISO 527-2/5
%
6
elongation
屈服 3
ASTM D638
%
7
Bending modulus
-- 5
ISO 178
Mpa
3
Bending modulus
50.0 mm 跨距 4
ASTM D790
Mpa
3
Bending stress
屈服, 50.0 mm 跨距 4
ASTM D790
Mpa
1
Bending stress
-- 5, 6
ISO 178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/HU1000-1H1000
Vicat softening temperature
--
ASTM D15259
°C
2
Vicat softening temperature
--
ISO 306/B50
°C
2
Vicat softening temperature
--
ISO 306/B120
°C
2
Linear coefficient of thermal expansion
流动 : -20 到 150°C
ASTM E831
cm/cm/°C
5
Linear coefficient of thermal expansion
流动 : -40 到 40°C
ISO 11359-2
cm/cm/°C
5
Linear coefficient of thermal expansion
横向 : -20 到 150°C
ASTM E831
cm/cm/°C
5
Linear coefficient of thermal expansion
横向 : -40°C
ISO 11359-2
cm/cm/°C
5
Thermal deformation temperature under load
1.8 MPa, 未退火, 6.40 mm
ASTM D648
°C
2
Thermal deformation temperature under load
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 8
ISO 75-2/Af
°C
2
Electrical performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/HU1000-1H1000
Dielectric strength
1.60 mm, in Air
ASTM D149
KV/mm
3
Dielectric strength
1.60 mm, in Oil
ASTM D149
KV/mm
2
Volume resistivity
ASTM D257
ohms·cm
1
Impact performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/HU1000-1H1000
Non notched cantilever beam impact
23°C
ASTM D4812
J/m
1
Dart impact equipped with measuring instruments
23°C, Total Energy
ASTM D3763
J
0
flammability
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/HU1000-1H1000
Extreme Oxygen Index
ASTM D2863
%
4