PEI ULTEM™ HU2200-1H1000 SABIC INNOVATIVE US
126
- Unit Price:
- $4536 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant Food contact Filler: Glass fiber reinf 20% Filler by weight
- Application Areas:packing auto parts medicine Medical/nursing supplies
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 337°C/6.6kg | ASTMD1238 | 6.0 | g/10min |
| Melt volume flow rate | 360°C/5.0kg | ISO1133 | 7.00 | cm3/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.30to0.50 | % |
| Water absorption rate | Saturation,23°C | ISO62 | 1.0 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.55 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 6850 | Mpa |
| Bending modulus 5 | ISO178 | 6890 | Mpa | |
| Bending strength 5,6 | ISO178 | 228 | Mpa | |
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 225 | Mpa |
| Tensile modulus 2 | ASTMD638 | 6890 | Mpa | |
| Tensile modulus | ISO527-2/1 | 6890 | Mpa | |
| Tensile strength 3 | Yield | ASTMD638 | 131 | Mpa |
| Tensile stress | Yield | ISO527-2/5 | 131 | Mpa |
| Tensile strength 3 | Break | ASTMD638 | 131 | Mpa |
| Tensile stress | Break | ISO527-2/5 | 131 | Mpa |
| Elongation rate 3 | Yield | ASTMD638 | 4.0 | % |
| Tensile strain | Yield | ISO527-2/5 | 4.0 | % |
| Elongation rate 4 | Break | ASTMD638 | 4.0 | % |
| Tensile strain | Break | ISO527-2/5 | 4.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 208 | °C |
| Hot deformation temperature 9 | 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 205 | °C |
| Vicat softening temperature | ASTMD152510 | 220 | °C | |
| -- | ISO306/B50 | 212 | °C | |
| -- | ISO306/B120 | 218 | °C | |
| Linear coefficient of thermal expansion | MD：-20to150°C | ASTME831 | 2.5E-05 | cm/cm/°C |
| MD：23to150°C | ISO11359-2 | 2.5E-05 | cm/cm/°C | |
| TD：-40to150°C | ASTME831 | 5E-05 | cm/cm/°C | |
| TD：23to150°C | ISO11359-2 | 5E-05 | cm/cm/°C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 8.00 | J |
| Impact strength of simply supported beam gap 7 | 23°C | ISO179/1eA | 65 | kJ/m² |
| Suspended wall beam gap impact strength 8 | -30°C | ISO180/1A | 70 | kJ/m² |
| 23°C | ISO180/1A | 64 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.