Material Description

Technical Data Sheet

Material Description

Material Properties:Aging resistance High temperature resistan
Application Areas:Electrical applications household electrical appl
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	Flow 2	内部方法	0.40 到 0.60	%
	Shrinkage rate	Flow : 3.20 mm	内部方法	0.40 到 0.60	%
	Shrinkage rate	Shrinkage rate	Across Flow : 3.20 mm	内部方法	0.40 到 0.60	%
Water absorption rate	Saturation, 23°C	ISO 62	0.90	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.50	%
Melt flow rate	337°C/6.6 kg	ASTM D1238	14	g/10 min
Molten Volume Flow Rate (MVR)	360°C/5.0 kg	ISO 1133	14.0	cm3/10min

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus	-- 3	ASTM D638	6480	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	5300	Mpa
elongation	Yield 4	ASTM D638	2.0	%
	elongation	Yield	ISO 527-2/5	2.0	%
		elongation	Break 4	ASTM D638	2.0	%
		elongation	elongation	Break	ISO 527-2/5	2.0	%
Bending modulus	50.0 mm Span 5	ASTM D790	5580	Mpa
Bending modulus	Bending modulus	-- 6	ISO 178	5500	Mpa
Tensile strength	Yield 4	ASTM D638	94.0	Mpa
	Tensile strength	Yield	ISO 527-2/5	80.0	Mpa
		Tensile strength	Break 4	ASTM D638	94.0	Mpa
		Tensile strength	Tensile strength	Break	ISO 527-2/5	80.0	Mpa
Bending stress	-- 6, 7	ISO 178	145	Mpa
Bending stress	Bending stress	Yield, 50.0 mm Span 5	ASTM D790	156	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
thermal conductivity		ISO 8302	0.32	W/m/K
Vicat softening temperature	--	ASTM D152510	216	°C
	Vicat softening temperature	--	ISO 306/B50	211	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	213	°C
Linear coefficient of thermal expansion	Flow : -40 to 150°C	ASTM E831	3.2E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Flow : 23 to 150°C	ISO 11359-2	3.2E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow : -40 to 150°C	ASTM E831	3.5E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 150°C	ISO 11359-2	3.5E-5	cm/cm/°C
Thermal deformation temperature under load	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	204	°C
	Thermal deformation temperature under load	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	206	°C
		Thermal deformation temperature under load	0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span 9	ISO 75-2/Bf	204	°C
			Thermal deformation temperature under load	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	199	°C
				Thermal deformation temperature under load	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	202	°C
				Thermal deformation temperature under load	Thermal deformation temperature under load	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 9	ISO 75-2/Af	192	°C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过

Electrical performance	Test Method	Test Result
Compared to the Leakage Tracking Index (CTI)	UL 746	PLC 4
Hot wire ignition (HWI)	UL 746	PLC 4
High Voltage Arc Traceability Rate (HVTR)	UL 746	PLC 4
High arc combustion index (HAI) 12	UL 746	PLC 4
Arc resistance 11	ASTM D495	PLC 5

injection	Test Result	Unit
drying temperature	150	°C
Suggested maximum moisture content	0.020	%
Processing (melt) temperature	350 到 400	°C
Mold temperature	135 到 165	°C
drying time	4.0 到 6.0	hr
Suggested injection volume	40 到 60	%
Temperature at the rear of the barrel	330 到 400	°C
Temperature in the middle of the barrel	340 到 400	°C
Temperature at the front of the material cylinder	345 到 400	°C
Spray nozzle temperature	345 到 400	°C
Back pressure	0.300 到 0.700	Mpa
Screw speed	40 到 70	rpm
Exhaust hole depth	0.025 到 0.076	mm

Impact performance	Test Condition	Test Method	Test Result	Unit
Simple supported beam without notch impact strength 8	-30°C	ISO 179/1eU	25	kJ/m²
Simple supported beam without notch impact strength 8	Simple supported beam without notch impact strength 8	23°C	ISO 179/1eU	25	kJ/m²
Impact strength of simply supported beam gap 8	-30°C	ISO 179/1eA	4.0	kJ/m²
Impact strength of simply supported beam gap 8	Impact strength of simply supported beam gap 8	23°C	ISO 179/1eA	5.0	kJ/m²
Non notched cantilever beam impact	23°C	ASTM D4812	330	J/m
	Non notched cantilever beam impact	-30°C 9	ISO 180/1U	25	kJ/m²
	Non notched cantilever beam impact	Non notched cantilever beam impact	23°C 9	ISO 180/1U	25	kJ/m²
Dart impact equipped with measuring instruments	23°C, Total Energy	ASTM D3763	15.0	J

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.40 mm	UL 94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.