Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI 2312EPR-1000 SABIC INNOVATIVE US
ULTEM™
Electrical applications、household electrical appl
Aging resistance、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/2312EPR-1000
Melt flow rate
337°C/6.6 kg
ASTM D1238
g/10 min
1
Molten Volume Flow Rate (MVR)
360°C/5.0 kg
ISO 1133
cm3/10min
1
Shrinkage rate
横向流动 : 3.20 mm
内部方法
%
0
Shrinkage rate
流动 : 3.20 mm
内部方法
%
0
Shrinkage rate
流动 2
内部方法
%
0
Water absorption rate
平衡, 23°C, 50% RH
ISO 62
%
0
Water absorption rate
饱和, 23°C
ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/2312EPR-1000
Tensile strength
断裂
ISO 527-2/5
Mpa
8
Tensile strength
断裂 4
ASTM D638
Mpa
9
Tensile strength
屈服
ISO 527-2/5
Mpa
8
Tensile strength
屈服 4
ASTM D638
Mpa
9
Tensile modulus
--
ISO 527-2/1
Mpa
5
Tensile modulus
-- 3
ASTM D638
Mpa
6
elongation
断裂
ISO 527-2/5
%
2
elongation
断裂 4
ASTM D638
%
2
elongation
屈服
ISO 527-2/5
%
2
elongation
屈服 4
ASTM D638
%
2
Bending modulus
-- 6
ISO 178
Mpa
5
Bending modulus
50.0 mm 跨距 5
ASTM D790
Mpa
5
Bending stress
屈服, 50.0 mm 跨距 5
ASTM D790
Mpa
1
Bending stress
-- 6, 7
ISO 178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/2312EPR-1000
thermal conductivity
ISO 8302
W/m/K
0
Vicat softening temperature
--
ASTM D152510
°C
2
Vicat softening temperature
--
ISO 306/B50
°C
2
Vicat softening temperature
--
ISO 306/B120
°C
2
Linear coefficient of thermal expansion
流动 : -40 到 150°C
ASTM E831
cm/cm/°C
3
Linear coefficient of thermal expansion
流动 : 23 到 150°C
ISO 11359-2
cm/cm/°C
3
Linear coefficient of thermal expansion
横向 : -40 到 150°C
ASTM E831
cm/cm/°C
3
Linear coefficient of thermal expansion
横向 : 23 到 150°C
ISO 11359-2
cm/cm/°C
3
Thermal deformation temperature under load
0.45 MPa, 未退火, 3.20 mm
ASTM D648
°C
2
Thermal deformation temperature under load
0.45 MPa, 未退火, 6.40 mm
ASTM D648
°C
2
Thermal deformation temperature under load
0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 9
ISO 75-2/Bf
°C
2
Thermal deformation temperature under load
1.8 MPa, 未退火, 3.20 mm
ASTM D648
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 6.40 mm
ASTM D648
°C
2
Thermal deformation temperature under load
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 9
ISO 75-2/Af
°C
1
Impact performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/2312EPR-1000
Impact strength of simply supported beam gap 8
23°C
ISO 179/1eA
kJ/m²
5
Impact strength of simply supported beam gap 8
-30°C
ISO 179/1eA
kJ/m²
4
Simple supported beam without notch impact strength 8
23°C
ISO 179/1eU
kJ/m²
2
Simple supported beam without notch impact strength 8
-30°C
ISO 179/1eU
kJ/m²
2
Non notched cantilever beam impact
23°C
ASTM D4812
J/m
3
Non notched cantilever beam impact
-30°C 9
ISO 180/1U
kJ/m²
2
Non notched cantilever beam impact
23°C 9
ISO 180/1U
kJ/m²
2
Dart impact equipped with measuring instruments
23°C, Total Energy
ASTM D3763
J
1