PEI ULTEM™ 2212EPR-1000 SABIC INNOVATIVE US
133
- Unit Price:
- $16950 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 11MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Middle flow
- Application Areas:Electrical equipment Home appliance components Automotive Interior Parts Monitor
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Flow : 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
| Across Flow : 3.20 mm | 内部方法 | 0.50 到 0.70 | % | |
| Melt flow rate | 337°C/6.6 kg | ASTM D1238 | 15 | g/10 min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending modulus | 50.0 mm Span 3 | ASTM D790 | 5510 | Mpa |
| 100 mm Span 4 | ASTM D790 | 5100 | Mpa | |
| bending strength | Yield, 50.0 mm Span 3 | ASTM D790 | 172 | Mpa |
| Break, 100 mm Span 4 | ASTM D790 | 172 | Mpa | |
| Tensile strength 2 | Yield | ASTM D638 | 107 | Mpa |
| Break | ASTM D638 | 107 | Mpa | |
| Elongation rate 2 | Yield | ASTM D638 | 3.0 | % |
| Break | ASTM D638 | 3.0 | % | |
| Tensile modulus 1 | ASTM D638 | 5790 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat softening temperature | ASTM D15255 | 210 | °C | |
| Thermal deformation temperature under load | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 210 | °C |
| 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 212 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 205 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 207 | °C | |
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ASTM E831 | 3.6E-5 | cm/cm/°C |
| Across Flow : -40 to 40°C | ASTM E831 | 7.2E-5 | cm/cm/°C | |
| RTI | UL 746 | 105 | °C | |
| RTI Imp | UL 746 | 105 | °C | |
| RTI Elec | UL 746 | 105 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 4 | ||
| High arc combustion index (HAI) 7 | UL 746 | PLC 4 | ||
| Hot wire ignition (HWI) | UL 746 | PLC 1 | ||
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 4 | ||
| Arc resistance 6 | ASTM D495 | PLC 5 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Non notched cantilever beam impact | 23°C | ASTM D4812 | 480 | J/m |
| Dart impact equipped with measuring instruments | 23°C, Total Energy | ASTM D3763 | 12.0 | J |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.40 mm | UL 94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.