Melt flow rate

337°C/6.6 kg

ASTM D1238

g/10 min

1

Shrinkage rate

流动 : 3.20 mm

内部方法

%

0

Shrinkage rate

横向流动 : 3.20 mm

内部方法

%

0

Tensile strength 2

屈服

ASTM D638

Mpa

1

Tensile strength 2

断裂

ASTM D638

Mpa

1

Tensile modulus 1

ASTM D638

Mpa

5

Elongation rate 2

屈服

ASTM D638

%

3

Elongation rate 2

断裂

ASTM D638

%

3

Bending modulus

50.0 mm 跨距 3

ASTM D790

Mpa

5

Bending modulus

100 mm 跨距 4

ASTM D790

Mpa

5

bending strength

屈服, 50.0 mm 跨距 3

ASTM D790

Mpa

1

bending strength

断裂, 100 mm 跨距 4

ASTM D790

Mpa

1

RTI

UL 746

°C

1

RTI Elec

UL 746

°C

1

RTI Imp

UL 746

°C

1

Vicat softening temperature

ASTM D15255

°C

2

Linear coefficient of thermal expansion

流动 : -40 到 40°C

ASTM E831

cm/cm/°C

3

Linear coefficient of thermal expansion

横向 : -40 到 40°C

ASTM E831

cm/cm/°C

7

Thermal deformation temperature under load

0.45 MPa, 未退火, 3.20 mm

ASTM D648

°C

2

Thermal deformation temperature under load

0.45 MPa, 未退火, 6.40 mm

ASTM D648

°C

2

Thermal deformation temperature under load

1.8 MPa, 未退火, 3.20 mm

ASTM D648

°C

2

Thermal deformation temperature under load

1.8 MPa, 未退火, 6.40 mm

ASTM D648

°C

2

Non notched cantilever beam impact

23°C

ASTM D4812

J/m

4

Dart impact equipped with measuring instruments

23°C, Total Energy

ASTM D3763

J

1