PEI ULTEM™ UF5011S-1000 SABIC INNOVATIVE US

136

Unit Price:
$23008 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Aging resistance High temperature resistan
Application Areas:Electrical applications household electrical appl
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	MD2	内部方法	0.40到0.70	%
	Shrinkage rate	MD:3.20mm	内部方法	0.40到0.70	%
	Shrinkage rate	Shrinkage rate	TD:3.20mm	内部方法	0.40到0.70	%
Water absorption rate	Saturation,23°C	ISO62	1.2	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO62	0.20	%
Melt volume flow rate	360°C/5.0kg	ISO1133	20.0	cm3/10min
Melt mass flow rate	337°C/6.6kg	ASTMD1238	11	g/10min

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile strength	Break	ISO527-2/5	85.0	Mpa
	Tensile strength	Break4	ASTMD638	75.0	Mpa
		Tensile strength	Yield	ISO527-2/5	100	Mpa
		Tensile strength	Tensile strength	Yield4	ASTMD638	100	Mpa
Bending stress	Yield,50.0mmSpan5	ASTMD790	138	Mpa
Bending stress	Bending stress	--6,7	ISO178	110	Mpa
Tensile modulus	--3	ASTMD638	2900	Mpa
Tensile modulus	Tensile modulus	--	ISO527-2/1	2900	Mpa
elongation	Break	ISO527-2/5	50	%
	elongation	Break4	ASTMD638	60	%
		elongation	Yield	ISO527-2/5	8.0	%
		elongation	elongation	Yield4	ASTMD638	8.0	%
Bending modulus	--6	ISO178	2900	Mpa
Bending modulus	Bending modulus	50.0mmSpan5	ASTMD790	3100	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	1.8MPa,Unannealed,100mmSpan10	ISO75-2/Ae	200	°C
	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan11	ISO75-2/Af	198	°C
		Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTMD648	213	°C
			Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTMD648	216	°C
				Hot deformation temperature	0.45MPa,Unannealed,100mmSpan10	ISO75-2/Be	210	°C
					Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan11	ISO75-2/Bf	208	°C
						Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTMD648	201	°C
						Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTMD648	204	°C
Linear coefficient of thermal expansion	MD:-40to150°C	ASTME831	5.5E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD:23to150°C	ISO11359-2	5.5E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD:-40to150°C	ASTME831	5.5E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:23to150°C	ISO11359-2	5.5E-05	cm/cm/°C
Vicat softening temperature	--	ASTMD152512	227	°C
	Vicat softening temperature	--	ISO306/A50	220	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO306/B50,ISO306/B120	215	°C
thermal conductivity		ASTMC177	0.31	W/m/K
BallPressure Test	125°C	IEC60695-10-2	通过

Electrical performance	Test Condition	Test Method	Test Result	Unit
Leakage Trace Index	SolutionB	IEC60112	100	V
Leakage Trace Index	Leakage Trace Index	--	IEC60112	150	V
Dissipation factor	50Hz	ASTMD150,IEC60250	2.1E-03
Dissipation factor	Dissipation factor	60Hz	ASTMD150,IEC60250	2.1E-03
Dielectric strength	3.20mm,inOil	ASTMD149	18	KV/mm
Dielectric strength	Dielectric strength	3.20mm,in Oil	IEC60243-1	18	KV/mm
Surface resistivity		IEC60093	>1.0E+15	ohms
Dielectric constant	50Hz	ASTMD150	3.20
Dielectric constant	Dielectric constant	60Hz	ASTMD150	3.20
Volume resistivity		IEC60093	2.5E+15	ohms·cm

Impact performance	Test Condition	Test Method	Test Result	Unit
Cantilever beam without notch impact strength	23°C9	ISO180/1U	无断裂
	Cantilever beam without notch impact strength	-30°C9	ISO180/1U	无断裂
	Cantilever beam without notch impact strength	Cantilever beam without notch impact strength	23°C	ASTMD4812	2100	J/m
Dart impact equipped with measuring instruments	23°C,TotalEnergy	ASTMD3763	30.0	J
Impact strength of simply supported beam gap 8	23°C	ISO179/1eA	7.0	kJ/m²
Impact strength of simply supported beam gap 8	Impact strength of simply supported beam gap 8	-30°C	ISO179/1eA	7.0	kJ/m²
Reverse notch impact	3.20mm	ASTMD256	2100	J/m
Simple supported beam without notch impact strength 8	23°C	ISO179/1eU	无断裂
Simple supported beam without notch impact strength 8	Simple supported beam without notch impact strength 8	-30°C	ISO179/1eU	无断裂

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.