Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI UF5011S-1000 SABIC INNOVATIVE US
ULTEM™
Electrical applications、household electrical appl
Aging resistance、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/UF5011S-1000
Melt volume flow rate
360°C/5.0kg
ISO1133
cm3/10min
2
Melt mass flow rate
337°C/6.6kg
ASTMD1238
g/10min
1
Shrinkage rate
MD2
内部方法
%
0
Shrinkage rate
MD:3.20mm
内部方法
%
0
Shrinkage rate
TD:3.20mm
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
1
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/UF5011S-1000
Tensile strength
屈服4
ASTMD638
Mpa
1
Tensile strength
屈服
ISO527-2/5
Mpa
1
Tensile strength
断裂4
ASTMD638
Mpa
7
Tensile strength
断裂
ISO527-2/5
Mpa
8
Tensile modulus
--3
ASTMD638
Mpa
2
Tensile modulus
--
ISO527-2/1
Mpa
2
elongation
屈服4
ASTMD638
%
8
elongation
屈服
ISO527-2/5
%
8
elongation
断裂4
ASTMD638
%
6
elongation
断裂
ISO527-2/5
%
5
Bending modulus
50.0mm跨距5
ASTMD790
Mpa
3
Bending modulus
--6
ISO178
Mpa
2
Bending stress
--6,7
ISO178
Mpa
1
Bending stress
屈服,50.0mm跨距5
ASTMD790
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/UF5011S-1000
thermal conductivity
ASTMC177
W/m/K
0
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
2
Hot deformation temperature
0.45MPa,未退火,6.40mm
ASTMD648
°C
2
Hot deformation temperature
0.45MPa,未退火,100mm跨距10
ISO75-2/Be
°C
2
Hot deformation temperature
0.45MPa,未退火,64.0mm跨距11
ISO75-2/Bf
°C
2
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
2
Hot deformation temperature
1.8MPa,未退火,6.40mm
ASTMD648
°C
2
Hot deformation temperature
1.8MPa,未退火,100mm跨距10
ISO75-2/Ae
°C
2
Hot deformation temperature
1.8MPa,未退火,64.0mm跨距11
ISO75-2/Af
°C
1
Vicat softening temperature
--
ASTMD152512
°C
2
Vicat softening temperature
--
ISO306/A50
°C
2
Vicat softening temperature
--
ISO306/B50,ISO306/B120
°C
2
Linear coefficient of thermal expansion
MD:-40到150°C
ASTME831
cm/cm/°C
5
Linear coefficient of thermal expansion
MD:23到150°C
ISO11359-2
cm/cm/°C
5
Linear coefficient of thermal expansion
TD:-40到150°C
ASTME831
cm/cm/°C
5
Linear coefficient of thermal expansion
TD:23到150°C
ISO11359-2
cm/cm/°C
5
Electrical performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/UF5011S-1000
Surface resistivity
IEC60093
ohms
>
Dielectric strength
3.20mm,inOil
ASTMD149
KV/mm
1
Dielectric strength
3.20mm,在油中
IEC60243-1
KV/mm
1
Leakage Trace Index
--
IEC60112
V
1
Leakage Trace Index
解决方案B
IEC60112
V
1
Volume resistivity
IEC60093
ohms·cm
2
Impact performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/UF5011S-1000
Reverse notch impact
3.20mm
ASTMD256
J/m
2
Impact strength of simply supported beam gap 8
-30°C
ISO179/1eA
kJ/m²
7
Impact strength of simply supported beam gap 8
23°C
ISO179/1eA
kJ/m²
7
Cantilever beam without notch impact strength
23°C
ASTMD4812
J/m
2
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
3