PET Rynite® FR515 BK DUPONT SHENZHEN
86
- Unit Price:
- $4123 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant enhance Filler: Glass fiber reinf 15% filler by weight
- Application Areas:Electrical field Electrical enclosure Electronic field
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD2 | ISO294-4 | 1.2 | % |
| TD | ISO294-4 | 0.80 | % | |
| MD | ISO294-4 | 0.30 | % | |
| MD2 | ISO294-4 | 0.50 | % | |
| Top out temperature | 170 | °C | ||
| Melt volume flow rate | 280°C/2.16kg | ISO1133 | 6.00 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending stress | ISO178 | 170 | Mpa | |
| Tensile stress | Break | ISO527-2 | 107 | Mpa |
| Tensile strain | Break | ISO527-2 | 2.6 | % |
| Tensile modulus | ISO527-2 | 6800 | Mpa | |
| Bending modulus | ISO178 | 5940 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 200 | °C |
| 0.45MPa,Unannealed | ISO75-2/B | 240 | °C | |
| Linear coefficient of thermal expansion | MD：-- | ISO11359-2 | 1.8E-05 | cm/cm/°C |
| MD：-40to23°C | ISO11359-2 | 3.3E-05 | cm/cm/°C | |
| MD：55to160°C | ISO11359-2 | 1.2E-05 | cm/cm/°C | |
| TD：-- | ISO11359-2 | 8.8E-05 | cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 7E-05 | cm/cm/°C | |
| TD：55to160°C | ISO11359-2 | 1.1E-04 | cm/cm/°C | |
| Melting temperature 5 | ISO11357-3 | 254 | °C | |
| Vicat softening temperature | ISO306/B50 | 210 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compared to the anti leakage trace index | CTI | UL746 | PLC3 | |
| Dielectric strength | IEC60243-1 | 34 | KV/mm | |
| Dissipation factor | 100Hz | IEC60250 | 9E-03 | |
| 1MHz | IEC60250 | 0.015 | ||
| Relative permittivity | 100Hz | IEC60250 | 3.80 | |
| 1MHz | IEC60250 | 3.50 | ||
| Leakage Trace Index | IEC60112 | 200 | V | |
| Surface resistivity | IEC60093 | 1E+13 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -40°C | ISO179/1eU | 20 | kJ/m² |
| -30°C | ISO179/1eU | 35 | kJ/m² | |
| 23°C | ISO179/1eU | 40 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Sale | ISO2039-2 | 88 | |
| R-Sale | ISO2039-2 | 120 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | 5VA | |
| 0.9mm | IEC60695-11-10,-20 | V-0 | ||
| 1.5mm | IEC60695-11-10,-20 | 5VA | ||
| 0.9mm | UL94 | V-0 | ||
| Extreme Oxygen Index | ISO4589-2 | 32 | % | |
| FMVSS flammability | FMVSS302 | B | ||
| Burning rate 4 | 1.00mm | ISO3795 | <100 | mm/min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.