Melt volume flow rate

280°C/2.16kg

ISO1133

cm3/10min

6

Shrinkage rate

TD2

ISO294-4

%

1

Shrinkage rate

TD

ISO294-4

%

0

Shrinkage rate

MD

ISO294-4

%

0

Shrinkage rate

MD2

ISO294-4

%

0

Tensile modulus

ISO527-2

Mpa

6

Tensile strain

断裂

ISO527-2

%

2

Tensile stress

断裂

ISO527-2

Mpa

1

Bending modulus

ISO178

Mpa

5

Bending stress

ISO178

Mpa

1

Hot deformation temperature

1.8MPa,未退火

ISO75-2/A

°C

2

Hot deformation temperature

0.45MPa,未退火

ISO75-2/B

°C

2

Melting temperature 5

ISO11357-3

°C

2

Vicat softening temperature

ISO306/B50

°C

2

Linear coefficient of thermal expansion

TD：55to160°C

ISO11359-2

cm/cm/°C

1

Linear coefficient of thermal expansion

TD：-40to23°C

ISO11359-2

cm/cm/°C

7

Linear coefficient of thermal expansion

TD：--

ISO11359-2

cm/cm/°C

8

Linear coefficient of thermal expansion

MD：55to160°C

ISO11359-2

cm/cm/°C

1

Linear coefficient of thermal expansion

MD：-40to23°C

ISO11359-2

cm/cm/°C

3

Linear coefficient of thermal expansion

MD：--

ISO11359-2

cm/cm/°C

1

Surface resistivity

IEC60093

ohms

1

Dielectric strength

IEC60243-1

KV/mm

3

Leakage Trace Index

IEC60112

V

2

Volume resistivity

IEC60093

ohms·cm

>

Impact strength of simply supported beam without notch

-40°C

ISO179/1eU

kJ/m²

2

Impact strength of simply supported beam without notch

-30°C

ISO179/1eU

kJ/m²

3

Impact strength of simply supported beam without notch

23°C

ISO179/1eU

kJ/m²

4

Extreme Oxygen Index

ISO4589-2

%

3

Burning rate 4

1.00mm

ISO3795

mm/min

<