PBT CELANEX® 2300GV3/20 CELANESE USA

121

Unit Price:
$4172 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High gloss
Application Areas:Electronic and electrical Automotive sector
Color:--
Grade:--

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO62	0.20	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO62	0.15	%
Shrinkage rate	TD	ISO294-4	1.0到1.3	%
Shrinkage rate	Shrinkage rate	MD	ISO294-4	0.40到0.50	%
Melt volume flow rate	250°C/2.16kg	ISO1133	20.0	cm3/10min
Melt volume flow rate	Melt volume flow rate	250°C/2.16kg	ISO1133	14.0	cm3/10min

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile creep modulus	1hr	ISO899-1	6200	Mpa
	Tensile creep modulus	1000hr	ISO899-1	4800	Mpa
		Tensile creep modulus	1hr	ISO899-1	3500	Mpa
		Tensile creep modulus	Tensile creep modulus	1000hr	ISO899-1	2400	Mpa
Bending stress	23°C	ISO178	170	Mpa
Bending stress	Bending stress	23°C	ISO178	86.0	Mpa
Tensile stress	Break	ISO527-2/1A/5	125	Mpa
Tensile stress	Tensile stress	Break	ISO527-2/1A/5	50.0	Mpa
Tensile strain	Break	ISO527-2/1A/5	4.0	%
Tensile strain	Tensile strain	Break	ISO527-2/1A/5	3.0	%
Tensile modulus		ISO527-2/1A/1	3500	Mpa
Tensile modulus	Tensile modulus		ISO527-2/1A/1	7400	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	220	°C
	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	195	°C
		Hot deformation temperature	8.0MPa,Unannealed	ISO75-2/C	100	°C
			Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	180	°C
			Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	70.0	°C
Melting temperature 3		ISO11357-3	225	°C
Vicat softening temperature		ISO306/B50	190	°C
Vicat softening temperature	Vicat softening temperature		ISO306/B50	215	°C
Linear coefficient of thermal expansion	MD	ISO11359-2	3.5E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO11359-2	1.1E-04	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC60093	>1.0E+15	ohms
Volume resistivity		IEC60093	>1.0E+15	ohms·cm
Dielectric strength		IEC60243-1	26	KV/mm
Dielectric strength	Dielectric strength		IEC60243-1	31	KV/mm
Relative permittivity	100Hz	IEC60250	4.20
	Relative permittivity	1MHz	IEC60250	4.10
		Relative permittivity	100Hz	IEC60250	4.40
		Relative permittivity	Relative permittivity	1MHz	IEC60250	4.20
Leakage Trace Index		IEC60112	225	V
Leakage Trace Index	Leakage Trace Index		IEC60112	350	V
Dissipation factor	100Hz	IEC60250	8.5E-03
	Dissipation factor	1MHz	IEC60250	0.018
		Dissipation factor	100Hz	IEC60250	1.6E-03
		Dissipation factor	Dissipation factor	1MHz	IEC60250	0.019

Filling analysis	Test Method	Test Result	Unit
SpecificHeatCapacity of Melt	内部方法	1840	J/kg/°C
ThermalConductivityofMelt	内部方法	0.16	W/m/K
Density of Melt	内部方法	1.230	g/cm³

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	34	kJ/m²
	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	34	kJ/m²
		Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	43	kJ/m²
		Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	46	kJ/m²

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.2mm	UL94	HB
	UL flame retardant rating	1.5mm	UL94	HB
		UL flame retardant rating	0.8mm	UL94	HB
		UL flame retardant rating	UL flame retardant rating	1.6mm	UL94	HB
Extreme Oxygen Index		ISO4589-2	21	%
Extreme Oxygen Index	Extreme Oxygen Index		ISO4589-2	20	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.