Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 2300GV3/20 CELANESE USA
CELANEX®
Electronic and electrical、Automotive sector
High gloss
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PBT/CELANESE USA/2300GV3/20
Melt volume flow rate
250°C/2.16kg
ISO1133
cm3/10min
2
Melt volume flow rate
250°C/2.16kg
ISO1133
cm3/10min
1
Shrinkage rate
TD
ISO294-4
%
1
Shrinkage rate
MD
ISO294-4
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PBT/CELANESE USA/2300GV3/20
Tensile modulus
ISO527-2/1A/1
Mpa
3
Tensile modulus
ISO527-2/1A/1
Mpa
7
Tensile creep modulus
1hr
ISO899-1
Mpa
6
Tensile creep modulus
1000hr
ISO899-1
Mpa
4
Tensile creep modulus
1hr
ISO899-1
Mpa
3
Tensile creep modulus
1000hr
ISO899-1
Mpa
2
Tensile strain
断裂
ISO527-2/1A/5
%
4
Tensile strain
断裂
ISO527-2/1A/5
%
3
Tensile stress
断裂
ISO527-2/1A/5
Mpa
1
Tensile stress
断裂
ISO527-2/1A/5
Mpa
5
Bending stress
23°C
ISO178
Mpa
8
Bending stress
23°C
ISO178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PBT/CELANESE USA/2300GV3/20
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
1
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
7
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
1
Hot deformation temperature
8.0MPa,未退火
ISO75-2/C
°C
1
Melting temperature 3
ISO11357-3
°C
2
Vicat softening temperature
ISO306/B50
°C
2
Vicat softening temperature
ISO306/B50
°C
1
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
3
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
1
Electrical performance
Test Condition
Test Method
Unit
PBT/CELANESE USA/2300GV3/20
Surface resistivity
IEC60093
ohms
>
Dielectric strength
IEC60243-1
KV/mm
2
Dielectric strength
IEC60243-1
KV/mm
3
Leakage Trace Index
IEC60112
V
3
Leakage Trace Index
IEC60112
V
2
Volume resistivity
IEC60093
ohms·cm
>
Filling analysis
Test Condition
Test Method
Unit
PBT/CELANESE USA/2300GV3/20
Density of Melt
内部方法
g/cm³
1
SpecificHeatCapacity of Melt
内部方法
J/kg/°C
1
ThermalConductivityofMelt
内部方法
W/m/K
0
Impact performance
Test Condition
Test Method
Unit
PBT/CELANESE USA/2300GV3/20
Impact strength of simply supported beam without notch
-30°C
ISO179/1eU
kJ/m²
4
Impact strength of simply supported beam without notch
-30°C
ISO179/1eU
kJ/m²
3
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
3
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
4
flammability
Test Condition
Test Method
Unit
PBT/CELANESE USA/2300GV3/20
Extreme Oxygen Index
ISO4589-2
%
2
Extreme Oxygen Index
ISO4589-2
%
2