Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant Electrical performance Filler: Glass fiber reinf 30% filler by weight
Application Areas:Electronic display Automotive External Parts
Color:--
Grade:Enhanced level

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Melt mass flow rate	250°C/2.16kg	ASTMD1238	13	g/10min
	Melt mass flow rate	250°C/5.0kg	ASTMD1238	67	g/10min
		Melt mass flow rate	265°C/5.0kg	ASTMD1238	90	g/10min
		Melt mass flow rate	Melt mass flow rate	266°C/5.0kg	ASTMD1238	90	g/10min
Melt volume flow rate	250°C/5.0kg	ISO1133	40.0	cm3/10min
Melt volume flow rate	Melt volume flow rate	265°C/5.0kg	ISO1133	65.0	cm3/10min
Shrinkage rate 3	MD	内部方法	0.10到0.30	%
Shrinkage rate 3	Shrinkage rate 3	TD	内部方法	0.40到0.70	%
Water absorption rate	Saturation,23°C	ISO62	0.25	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO62	0.070	%
Density/specific gravity		ASTMD792,ISO1183	1.67	g/cm³

Mechanical performance	Test Condition	Test Method	Test Result	Unit
elongation	Break5	ASTMD638	2.0	%
elongation	elongation	Break	ISO527-2/5	2.0	%
Bending modulus	50.0mmSpan6	ASTMD790	9000	Mpa
Bending modulus	Bending modulus	--7	ISO178	9600	Mpa
Bending stress	--7,8	ISO178	200	Mpa
	Bending stress	Yield,50.0mmSpan6	ASTMD790	200	Mpa
	Bending stress	Bending stress	Break,50.0mmSpan6	ASTMD790	200	Mpa
Fracture bending strain 9		ISO178	3.0	%
Tensile modulus	--4	ASTMD638	11500	Mpa
Tensile modulus	Tensile modulus	--	ISO527-2/1	11500	Mpa
Tensile strength	Yield5	ASTMD638	130	Mpa
	Tensile strength	Yield	ISO527-2/5	130	Mpa
		Tensile strength	Break5	ASTMD638	130	Mpa
		Tensile strength	Tensile strength	Break	ISO527-2/5	130	Mpa
elongation	Yield5	ASTMD638	2.0	%
elongation	elongation	Yield	ISO527-2/5	2.0	%

Thermal performance	Test Condition	Test Method	Test Result	Unit
Vicat softening temperature	--	ASTMD152514,ISO306/B50,ISO306/B120	205	°C
Vicat softening temperature	Vicat softening temperature	--	ASTMD152515,ISO306/A5015	220	°C
BallPressure Test	125°C	IEC60695-10-2	通过
Linear coefficient of thermal expansion	MD:-40to40°C	ISO11359-2	2.2E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD:23to80°C	ISO11359-2	1.6E-05	cm/cm/°C
		Linear coefficient of thermal expansion	MD:23to150°C	ISO11359-2	1.4E-05	cm/cm/°C
			Linear coefficient of thermal expansion	TD:-40to40°C	ISO11359-2	8.2E-05	cm/cm/°C
				Linear coefficient of thermal expansion	TD:23to80°C	ISO11359-2	1.2E-04	cm/cm/°C
				Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:23to150°C	ISO11359-2	1.3E-04	cm/cm/°C
RTIElec		UL746	130	°C
Evolution Calendar intelligent importer		UL746	130	°C
RTI		UL746	140	°C
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTMD648	220	°C
	Hot deformation temperature	0.45MPa,Unannealed,100mmSpan12	ISO75-2/Be	220	°C
		Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan13	ISO75-2/Bf	220	°C
			Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTMD648	205	°C
			Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan13	ISO75-2/Af	205	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Volume resistivity		ASTMD257,IEC60093	>1.0E+15	ohms·cm
Dielectric strength	0.800mm,in Oil	IEC60243-1	27	KV/mm
	Dielectric strength	1.60mm,in Oil	IEC60243-1	23	KV/mm
	Dielectric strength	Dielectric strength	3.20mm,in Oil	IEC60243-1	19	KV/mm
Dielectric constant	1MHz	ASTMD150,IEC60250	3.50
	Dielectric constant	50Hz	IEC60250	3.00
	Dielectric constant	Dielectric constant	60Hz	IEC60250	3.00
Dissipation factor	1MHz	ASTMD150,IEC60250	0.010
	Dissipation factor	50Hz	IEC60250	1E-03
	Dissipation factor	Dissipation factor	60Hz	IEC60250	1E-03
Compared to the anti leakage trace index	CTI	UL746	PLC2
Leakage Trace Index		IEC60112	250	V
High arc combustion index	HAI	UL746	PLC3
High voltage arc tracing rate	HVTR	UL746	PLC4
Hot wire ignition	HWI	UL746	PLC0
Surface resistivity		IEC60093	>1.0E+15	ohms

Filling analysis	Test Condition	Test Method	Test Result	Unit
Melt viscosity	260°C,1500sec^-1	ISO11443	115	Pa·s

Impact performance	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	-30°C10	ISO179/1eA	10	kJ/m²
	Charpy Notched Impact Strength	-30°C	ISO179/2C	9.0	kJ/m²
		Charpy Notched Impact Strength	23°C10	ISO179/1eA	10	kJ/m²
		Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/2C	11	kJ/m²
Impact strength of simply supported beam without notch	-30°C10	ISO179/1eU	55	kJ/m²
	Impact strength of simply supported beam without notch	-30°C	ISO179/2U	50	kJ/m²
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C10	ISO179/1eU,ISO179/2U	50	kJ/m²
Impact strength of cantilever beam gap	-30°C	ASTMD256	80	J/m
	Impact strength of cantilever beam gap	0°C	ASTMD256	80	J/m
		Impact strength of cantilever beam gap	23°C	ASTMD256	80	J/m
			Impact strength of cantilever beam gap	-30°C11	ISO180/1A	8.0	kJ/m²
				Impact strength of cantilever beam gap	0°C11	ISO180/1A	8.0	kJ/m²
				Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C11	ISO180/1A	8.0	kJ/m²
Cantilever beam without notch impact strength	-30°C	ASTMD4812	660	J/m
	Cantilever beam without notch impact strength	23°C	ASTMD4812	660	J/m
		Cantilever beam without notch impact strength	-30°C11	ISO180/1U	45	kJ/m²
		Cantilever beam without notch impact strength	Cantilever beam without notch impact strength	23°C11	ISO180/1U	45	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	R-Sale	ISO2039-2	118
Ball pressure hardness	H358/30	ISO2039-1	115	Mpa

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.75mm	UL94	V-0
Burning wire flammability index	3.0mm	IEC60695-2-12	960	°C
Extreme Oxygen Index		ISO4589-2	34	%

Supplementary Information	Test Condition	Test Method	Test Result	Unit
Filling material		ASTMD229	30	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.