Density/specific gravity

ASTMD792,ISO1183

g/cm³

1

Melt volume flow rate

250°C/5.0kg

ISO1133

cm3/10min

4

Melt volume flow rate

265°C/5.0kg

ISO1133

cm3/10min

6

Melt mass flow rate

250°C/2.16kg

ASTMD1238

g/10min

1

Melt mass flow rate

250°C/5.0kg

ASTMD1238

g/10min

6

Melt mass flow rate

265°C/5.0kg

ASTMD1238

g/10min

9

Melt mass flow rate

266°C/5.0kg

ASTMD1238

g/10min

9

Shrinkage rate 3

MD

内部方法

%

0

Shrinkage rate 3

TD

内部方法

%

0

Water absorption rate

饱和,23°C

ISO62

%

0

Water absorption rate

平衡,23°C,50%RH

ISO62

%

0

Fracture bending strain 9

ISO178

%

3

Tensile strength

屈服5

ASTMD638

Mpa

1

Tensile strength

屈服

ISO527-2/5

Mpa

1

Tensile strength

断裂5

ASTMD638

Mpa

1

Tensile strength

断裂

ISO527-2/5

Mpa

1

Tensile modulus

--4

ASTMD638

Mpa

1

Tensile modulus

--

ISO527-2/1

Mpa

1

elongation

屈服5

ASTMD638

%

2

elongation

屈服

ISO527-2/5

%

2

elongation

断裂5

ASTMD638

%

2

elongation

断裂

ISO527-2/5

%

2

Bending modulus

50.0mm跨距6

ASTMD790

Mpa

9

Bending modulus

--7

ISO178

Mpa

9

Bending stress

--7,8

ISO178

Mpa

2

Bending stress

屈服,50.0mm跨距6

ASTMD790

Mpa

2

Bending stress

断裂,50.0mm跨距6

ASTMD790

Mpa

2

RTI

UL746

°C

1

RTIElec

UL746

°C

1

Evolution Calendar intelligent importer

UL746

°C

1

Hot deformation temperature

0.45MPa,未退火,3.20mm

ASTMD648

°C

2

Hot deformation temperature

0.45MPa,未退火,100mm跨距12

ISO75-2/Be

°C

2

Hot deformation temperature

0.45MPa,未退火,64.0mm跨距13

ISO75-2/Bf

°C

2

Hot deformation temperature

1.8MPa,未退火,3.20mm

ASTMD648

°C

2

Hot deformation temperature

1.8MPa,未退火,64.0mm跨距13

ISO75-2/Af

°C

2

Vicat softening temperature

--

ASTMD152514,ISO306/B50,ISO306/B120

°C

2

Vicat softening temperature

--

ASTMD152515,ISO306/A5015

°C

2

Linear coefficient of thermal expansion

MD:-40到40°C

ISO11359-2

cm/cm/°C

2

Linear coefficient of thermal expansion

MD:23到80°C

ISO11359-2

cm/cm/°C

1

Linear coefficient of thermal expansion

MD:23到150°C

ISO11359-2

cm/cm/°C

1

Linear coefficient of thermal expansion

TD:-40到40°C

ISO11359-2

cm/cm/°C

8

Linear coefficient of thermal expansion

TD:23到80°C

ISO11359-2

cm/cm/°C

1

Linear coefficient of thermal expansion

TD:23到150°C

ISO11359-2

cm/cm/°C

1

Surface resistivity

IEC60093

ohms

>

Dielectric strength

0.800mm,在油中

IEC60243-1

KV/mm

2

Dielectric strength

1.60mm,在油中

IEC60243-1

KV/mm

2

Dielectric strength

3.20mm,在油中

IEC60243-1

KV/mm

1

Leakage Trace Index

IEC60112

V

2

Volume resistivity

ASTMD257,IEC60093

ohms·cm

>

Melt viscosity

260°C,1500sec^-1

ISO11443

Pa·s

1

Charpy Notched Impact Strength

-30°C10

ISO179/1eA

kJ/m²

1

Charpy Notched Impact Strength

-30°C

ISO179/2C

kJ/m²

9

Charpy Notched Impact Strength

23°C10

ISO179/1eA

kJ/m²

1

Charpy Notched Impact Strength

23°C

ISO179/2C

kJ/m²

1

Impact strength of simply supported beam without notch

-30°C10

ISO179/1eU

kJ/m²

5

Impact strength of simply supported beam without notch

-30°C

ISO179/2U

kJ/m²

5

Impact strength of simply supported beam without notch

23°C10

ISO179/1eU,ISO179/2U

kJ/m²

5

Impact strength of cantilever beam gap

-30°C

ASTMD256

J/m

8

Impact strength of cantilever beam gap

0°C

ASTMD256

J/m

8

Impact strength of cantilever beam gap

23°C

ASTMD256

J/m

8

Impact strength of cantilever beam gap

-30°C11

ISO180/1A

kJ/m²

8

Impact strength of cantilever beam gap

0°C11

ISO180/1A

kJ/m²

8

Impact strength of cantilever beam gap

23°C11

ISO180/1A

kJ/m²

8

Cantilever beam without notch impact strength

-30°C

ASTMD4812

J/m

6

Cantilever beam without notch impact strength

23°C

ASTMD4812

J/m

6

Cantilever beam without notch impact strength

-30°C11

ISO180/1U

kJ/m²

4

Cantilever beam without notch impact strength

23°C11

ISO180/1U

kJ/m²

4

Ball pressure hardness

H358/30

ISO2039-1

Mpa

1

Extreme Oxygen Index

ISO4589-2

%

3

Burning wire flammability index

3.0mm

IEC60695-2-12

°C

9

Filling material

ASTMD229

%

3