PBT VALOX™ VX5022 SABIC INNOVATIVE US
121
- Unit Price:
- $8073 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low warpage Anti deformation Filler: Glass fiber reinf 20% filler by weight
- Application Areas:Automotive components
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density/specific gravity | ASTMD792,ISO1183 | 1.39 | g/cm³ | |
| Melt mass flow rate | 250°C/2.16kg | ASTMD1238 | 16 | g/10min |
| 265°C/5.0kg | ASTMD1238 | 50 | g/10min | |
| 266°C/5.0kg | ASTMD1238 | 50 | g/10min | |
| Melt volume flow rate | 250°C/2.16kg | ISO1133 | 13.0 | cm3/10min |
| 250°C/5.0kg | ISO1133 | 28.0 | cm3/10min | |
| 265°C/5.0kg | ISO1133 | 40.0 | cm3/10min | |
| Shrinkage rate | MD1 | 内部方法 | 0.30到0.80 | % |
| MD:3.20mm | 内部方法 | 0.30到0.50 | % | |
| TD2 | 内部方法 | 0.50到0.90 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.10 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.060 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| --3 | ASTMD638 | 7300 | Mpa | |
| -- | ISO527-2/1 | 7100 | Mpa | |
| Surrender 4 | ASTMD638 | 125 | Mpa | |
| yield | ISO527-2/5 | 110 | Mpa | |
| Fracture 5 | ASTMD638 | 125 | Mpa | |
| crack | ISO527-2/5 | 110 | Mpa | |
| Surrender 6 | ASTMD638 | 3.0 | % | |
| yield | ISO527-2/5 | 3.0 | % | |
| Fracture 7 | ASTMD638 | 3.0 | % | |
| crack | ISO527-2/5 | 3.0 | % | |
| 50.0mm span 8 | ASTMD790 | 5800 | Mpa | |
| --9 | ISO178 | 6300 | Mpa | |
| --10 | ISO178 | 150 | Mpa | |
| Yield, 50.0mm span 11 | ASTMD790 | 145 | Mpa | |
| Fracture bending strain 12 | ISO178 | 3.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 1.8MPa, unannealed, 3.20mm | ASTMD648 | 120 | °C | |
| 1.8MPa, unannealed, 64.0mm span 23 | ISO75-2/Af | 120 | °C | |
| -- | ASTMD1525,ISO306/B50,ISO306/B12024 | 145 | °C | |
| ASTMD1525,ISO306/A501325 | 200 | °C | ||
| BallPressure Test | 125°C | IEC60695-10-2 | Pass | |
| Flow: -40 to 40 ° C | ASTME831 | 4E-05 | cm/cm/°C | |
| ISO11359-2 | 2.5E-05 | cm/cm/°C | ||
| Flow: 23 to 60 ° C | ISO11359-2 | 4E-05 | cm/cm/°C | |
| Flow: 23 to 80 ° C | ISO11359-2 | 4E-05 | cm/cm/°C | |
| Flow: 23 to 150 ° C | ISO11359-2 | 2.4E-05 | cm/cm/°C | |
| Horizontal: -40 to 40 ° C | ASTME831 | 1E-04 | cm/cm/°C | |
| ISO11359-2 | 6.9E-05 | cm/cm/°C | ||
| Horizontal: 23 to 60 ° C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| Horizontal: 23 to 80 ° C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| Horizontal: 23 to 150 ° C | ISO11359-2 | 1.1E-04 | cm/cm/°C | |
| 0.45MPa, unannealed, 3.20mm | ASTMD648 | 180 | °C | |
| 0.45MPa, unannealed, 64.0mm span 22 | ISO75-2/Bf | 180 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 0.800mm, in oil | IEC60243-1 | 31 | KV/mm | |
| 1.60mm, in oil | IEC60243-1 | 28 | KV/mm | |
| 3.20mm, in oil | IEC60243-1 | 16 | KV/mm | |
| 1MHz | ASTMD150,IEC60250 | 3.30 | ||
| 50Hz | IEC60250 | 3.10 | ||
| 60Hz | IEC60250 | 3.10 | ||
| 100Hz | IEC60250 | 3.30 | ||
| 1MHz | ASTMD150,IEC60250 | 0.014 | ||
| 50Hz | IEC60250 | 1E-03 | ||
| 60Hz | IEC60250 | 1E-03 | ||
| 100Hz | IEC60250 | 1E-03 | ||
| Leakage Trace Index | -- | IEC60112 | 200 | V |
| SolutionB | IEC60112 | 100 | V | |
| High arc combustion index | HAI | UL746 | PLC0 | |
| Hot wire ignition | HWI | UL746 | PLC0 | |
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | ASTMD257,IEC60093 | >1.0E+15 | ohms·cm | |
| 0.800mm,inOil | ASTMD149 | 31 | KV/mm | |
| 1.60mm,inOil | ASTMD149 | 28 | KV/mm | |
| 3.20mm, inoil | ASTMD149 | 16 | KV/mm |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt viscosity | 260°C,1500sec^-1 | ISO11443 | 215 | Pa·s |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| -30°C | ISO179/2C | 9.0 | kJ/m² | |
| 23°C14 | ISO179/1eA | 6.5 | kJ/m² | |
| 23°C | ISO179/2C | 9.0 | kJ/m² | |
| -30°C15 | ISO179/1eU | 40 | kJ/m² | |
| -30°C | ISO179/2U | 50 | kJ/m² | |
| 23°C16 | ISO179/1eU | 40 | kJ/m² | |
| 23°C | ISO179/2U | 55 | kJ/m² | |
| -30°C | ASTMD256 | 80 | J/m | |
| 0°C | ASTMD256 | 80 | J/m | |
| 23°C | ASTMD256 | 80 | J/m | |
| -30°C13 | ISO179/1eA | 5.5 | kJ/m² | |
| -30°C17 | ISO180/1A | 6.0 | kJ/m² | |
| 0°C18 | ISO180/1A | 7.0 | kJ/m² | |
| 23°C19 | ISO180/1A | 7.0 | kJ/m² | |
| -30°C | ASTMD4812 | 650 | J/m | |
| 23°C | ASTMD4812 | 650 | J/m | |
| -30°C20 | ISO180/1U | 35 | kJ/m² | |
| 23°C21 | ISO180/1U | 40 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 65.0 | J |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Sale | ISO2039-2 | 122 | |
| Ball pressure hardness | H358/30 | ISO2039-1 | 205 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.60mm,TestingbySABIC | UL94 | HB | |
| Burning wire flammability index | 1.00mm | IEC60695-2-12 | 750 | °C |
| 2.00mm | IEC60695-2-12 | 850 | °C | |
| Extreme Oxygen Index | ISO4589-2 | 23 | % |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Filling material | ASTMD229 | 20 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.