PBT VX5022 SABIC INNOVATIVE US
VALOX™
Automotive components
Low warpage、Anti deformation、Filler: Glass fiber reinf、20% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE US/VX5022
Density/specific gravity
ASTMD792,ISO1183
g/cm³
1
Melt volume flow rate
265°C/5.0kg
ISO1133
cm3/10min
4
Melt volume flow rate
250°C/5.0kg
ISO1133
cm3/10min
2
Melt volume flow rate
250°C/2.16kg
ISO1133
cm3/10min
1
Melt mass flow rate
266°C/5.0kg
ASTMD1238
g/10min
5
Melt mass flow rate
265°C/5.0kg
ASTMD1238
g/10min
5
Melt mass flow rate
250°C/2.16kg
ASTMD1238
g/10min
1
Shrinkage rate
TD2
内部方法
%
0
Shrinkage rate
MD:3.20mm
内部方法
%
0
Shrinkage rate
MD1
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE US/VX5022
--
ISO527-2/1
Mpa
7
--10
ISO178
Mpa
1
--3
ASTMD638
Mpa
7
50.0mm span 8
ASTMD790
Mpa
5
--9
ISO178
Mpa
6
crack
ISO527-2/5
%
3
crack
ISO527-2/5
Mpa
1
Fracture 5
ASTMD638
Mpa
1
Fracture 7
ASTMD638
%
3
Fracture bending strain 12
ISO178
%
3
yield
ISO527-2/5
%
3
yield
ISO527-2/5
Mpa
1
Yield, 50.0mm span 11
ASTMD790
Mpa
1
Surrender 4
ASTMD638
Mpa
1
Surrender 6
ASTMD638
%
3
Thermal performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE US/VX5022
--
ASTMD1525,ISO306/B50,ISO306/B12024
°C
1
--
ASTMD1525,ISO306/A501325
°C
2
0.45MPa, unannealed, 3.20mm
ASTMD648
°C
1
0.45MPa, unannealed, 64.0mm span 22
ISO75-2/Bf
°C
1
1.8MPa, unannealed, 3.20mm
ASTMD648
°C
1
1.8MPa, unannealed, 64.0mm span 23
ISO75-2/Af
°C
1
Horizontal: 23 to 150 ° C
ISO11359-2
cm/cm/°C
1
Horizontal: 23 to 60 ° C
ISO11359-2
cm/cm/°C
1
Horizontal: 23 to 80 ° C
ISO11359-2
cm/cm/°C
1
Horizontal: -40 to 40 ° C
ASTME831
cm/cm/°C
1
Horizontal: -40 to 40 ° C
ISO11359-2
cm/cm/°C
6
Flow: 23 to 150 ° C
ISO11359-2
cm/cm/°C
2
Flow: 23 to 60 ° C
ISO11359-2
cm/cm/°C
4
Flow: 23 to 80 ° C
ISO11359-2
cm/cm/°C
4
Flow: -40 to 40 ° C
ASTME831
cm/cm/°C
4
Flow: -40 to 40 ° C
ISO11359-2
cm/cm/°C
2
Electrical performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE US/VX5022
0.800mm,inOil
ASTMD149
KV/mm
3
0.800mm, in oil
IEC60243-1
KV/mm
3
1.60mm,inOil
ASTMD149
KV/mm
2
1.60mm, in oil
IEC60243-1
KV/mm
2
3.20mm, inoil
ASTMD149
KV/mm
1
3.20mm, in oil
IEC60243-1
KV/mm
1
Surface resistivity
IEC60093
ohms
>
Leakage Trace Index
--
IEC60112
V
2
Leakage Trace Index
解决方案B
IEC60112
V
1
Volume resistivity
ASTMD257,IEC60093
ohms·cm
>
Filling analysis
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE US/VX5022
Melt viscosity
260°C,1500sec^-1
ISO11443
Pa·s
2
Impact performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE US/VX5022
0°C
ASTMD256
J/m
8
0°C18
ISO180/1A
kJ/m²
7
23°C
ASTMD4812
J/m
6
23°C
ISO179/2C
kJ/m²
9
23°C
ISO179/2U
kJ/m²
5
23°C
ASTMD256
J/m
8
23°C14
ISO179/1eA
kJ/m²
6
23°C16
ISO179/1eU
kJ/m²
4
23°C19
ISO180/1A
kJ/m²
7
23°C21
ISO180/1U
kJ/m²
4
-30°C
ASTMD4812
J/m
6
-30°C
ISO179/2U
kJ/m²
5
-30°C
ASTMD256
J/m
8
-30°C
ISO179/2C
kJ/m²
9
-30°C13
ISO179/1eA
kJ/m²
5
-30°C15
ISO179/1eU
kJ/m²
4
-30°C17
ISO180/1A
kJ/m²
6
-30°C20
ISO180/1U
kJ/m²
3
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
6
hardness
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE US/VX5022
Ball pressure hardness
H358/30
ISO2039-1
Mpa
2
flammability
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE US/VX5022
Extreme Oxygen Index
ISO4589-2
%
2
Burning wire flammability index
1.00mm
IEC60695-2-12
°C
7
Burning wire flammability index
2.00mm
IEC60695-2-12
°C
8
Supplementary Information
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE US/VX5022
Filling material
ASTMD229
%
2