PPO NORYL™ V0150B-701 SABIC INNOVATIVE JAPAN
106
- Unit Price:
- $5838 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Dimensional stability Low water absorption Non enhanced Low temperature impact re
- Application Areas:Outdoor applications Solar junction box Shell
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTMD792 | 1.11 | g/cm³ | |
| ISO1183 | 1.11 | g/cm³ | ||
| Melt mass flow rate | 280°C/5.0kg | ASTMD1238 | 3.5 | g/10min |
| Melt volume flow rate | 300°C/5.0kg | ISO1133 | 10.0 | cm3/10min |
| Shrinkage rate | MD：--2 | 内部方法 | 0.50to0.70 | % |
| MD：3.20mm | 内部方法 | 0.50to0.70 | % | |
| Water absorption rate | 饱和,23°C | ISO62 | 0.18 | % |
| 平衡,23°C,50%RH | ISO62 | 0.060 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ASTMD638 | 2500 | Mpa | |
| ISO527-2/1 | 2500 | Mpa | ||
| Tensile strength | 屈服 | ASTMD638 | 70.0 | Mpa |
| Tensile stress | 屈服 | ISO527-2/50 | 70.0 | Mpa |
| tensile strength | Break | ASTMD638 | 60.0 | Mpa |
| Tensile stress | 断裂 | ISO527-2/50 | 55.0 | Mpa |
| elongation | 屈服 | ASTMD638 | 5.0 | % |
| Tensile strain | 屈服 | ISO527-2/50 | 4.0 | % |
| elongation | 断裂 | ASTMD638 | 7.0 | % |
| Tensile strain | 断裂 | ISO527-2/50 | 10 | % |
| Bending modulus | 50.0mmSpan | ASTMD790 | 2550 | Mpa |
| Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 105 | Mpa |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 35.0 | mg |
| Bending modulus | ISO178 | 2400 | Mpa | |
| bending strength | ISO178 | 110 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 140 | °C |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 135 | °C | |
| 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 130 | °C | |
| Vicat softening temperature | ASTMD152511 | 155 | °C | |
| -- | ISO306/A50 | 160 | °C | |
| -- | ISO306/B50 | 145 | °C | |
| -- | ISO306/B120 | 155 | °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 7.5E-05 | cm/cm/°C |
| MD：23到80°C | ISO11359-2 | 7E-05 | cm/cm/°C | |
| TD：-40到40°C | ASTME831 | 7.5E-05 | cm/cm/°C | |
| TD：23to80°C | ISO11359-2 | 9E-05 | cm/cm/°C | |
| thermal conductivity | ISO8302 | 0.27 | W/m/K | |
| RTI Elec | UL746 | 110 | °C | |
| RTI Imp | UL746 | 105 | °C | |
| RTI Str | UL746 | 115 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC60093 | 1E+15 | ohms·cm | |
| Dielectric strength | 0.800mm,在油中 | IEC60243-1 | 33 | KV/mm |
| 1.60mm,在油中 | IEC60243-1 | 26 | KV/mm | |
| 3.20mm,在油中 | IEC60243-1 | 16 | KV/mm | |
| Leakage Trace Index | IEC60112 | 250 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 5.0 | kJ/m² |
| 23°C | ISO179/1eA | 14 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ASTMD256 | 180 | J/m |
| 23°C | ASTMD256 | 330 | J/m | |
| -30°C | ISO180/1A | 5.0 | kJ/m² | |
| 23°C | ISO180/1A | 13 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 50.0 | J |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | H358/30 | ISO2039-1 | 113 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning wire flammability index | 1.0mm | IEC60695-2-12 | 960 | °C |
| Hot filament ignition temperature | 1.0mm | IEC60695-2-13 | 775 | °C |
| 2.0mm | IEC60695-2-13 | 775 | °C | |
| 3.0mm | IEC60695-2-13 | 775 | °C | |
| Extreme Oxygen Index | ISO4589-2 | 32 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.