PPO V0150B-701 SABIC INNOVATIVE JAPAN
NORYL™
Outdoor applications、Solar junction box、Shell
Dimensional stability、Low water absorption、Non enhanced、Low temperature impact re
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE JAPAN/V0150B-701
density
ASTMD792
g/cm³
1
density
ISO1183
g/cm³
1
Melt volume flow rate
300°C/5.0kg
ISO1133
cm3/10min
1
Melt mass flow rate
280°C/5.0kg
ASTMD1238
g/10min
3
Shrinkage rate
MD：--2
内部方法
%
0
Shrinkage rate
MD：3.20mm
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE JAPAN/V0150B-701
Flexural Strength
Yield,50.0mmSpan
ASTMD790
Mpa
1
Tensile strength
屈服
ASTMD638
Mpa
7
Tensile modulus
ASTMD638
Mpa
2
Tensile modulus
ISO527-2/1
Mpa
2
tensile strength
Break
ASTMD638
Mpa
6
Tensile strain
断裂
ISO527-2/50
%
1
Tensile strain
屈服
ISO527-2/50
%
4
Tensile stress
断裂
ISO527-2/50
Mpa
5
Tensile stress
屈服
ISO527-2/50
Mpa
7
elongation
屈服
ASTMD638
%
5
elongation
断裂
ASTMD638
%
7
Taber abraser
1000Cycles,1000g,CS-17转轮
内部方法
mg
3
Bending modulus
50.0mmSpan
ASTMD790
Mpa
2
Bending modulus
ISO178
Mpa
2
bending strength
ISO178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE JAPAN/V0150B-701
RTI Elec
UL746
°C
1
RTI Imp
UL746
°C
1
RTI Str
UL746
°C
1
thermal conductivity
ISO8302
W/m/K
0
Hot deformation temperature
0.45MPa,Unannealed,100mmSpan
ISO75-2/Be
°C
1
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,Unannealed,100mmSpan
ISO75-2/Ae
°C
1
Vicat softening temperature
ASTMD152511
°C
1
Vicat softening temperature
--
ISO306/A50
°C
1
Vicat softening temperature
--
ISO306/B50
°C
1
Vicat softening temperature
--
ISO306/B120
°C
1
Linear coefficient of thermal expansion
MD：-40到40°C
ASTME831
cm/cm/°C
7
Linear coefficient of thermal expansion
MD：23到80°C
ISO11359-2
cm/cm/°C
7
Linear coefficient of thermal expansion
TD：-40到40°C
ASTME831
cm/cm/°C
7
Linear coefficient of thermal expansion
TD：23to80°C
ISO11359-2
cm/cm/°C
9
Electrical performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE JAPAN/V0150B-701
Surface resistivity
IEC60093
ohms
>
Dielectric strength
0.800mm,在油中
IEC60243-1
KV/mm
3
Dielectric strength
1.60mm,在油中
IEC60243-1
KV/mm
2
Dielectric strength
3.20mm,在油中
IEC60243-1
KV/mm
1
Leakage Trace Index
IEC60112
V
2
Volume resistivity
IEC60093
ohms·cm
1
Impact performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE JAPAN/V0150B-701
Charpy Notched Impact Strength
-30°C
ISO179/1eA
kJ/m²
5
Charpy Notched Impact Strength
23°C
ISO179/1eA
kJ/m²
1
Impact strength of cantilever beam gap
-30°C
ASTMD256
J/m
1
Impact strength of cantilever beam gap
23°C
ASTMD256
J/m
3
Impact strength of cantilever beam gap
-30°C
ISO180/1A
kJ/m²
5
Impact strength of cantilever beam gap
23°C
ISO180/1A
kJ/m²
1
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
5
hardness
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE JAPAN/V0150B-701
Ball pressure hardness
H358/30
ISO2039-1
Mpa
1
flammability
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE JAPAN/V0150B-701
Extreme Oxygen Index
ISO4589-2
%
3
Hot filament ignition temperature
1.0mm
IEC60695-2-13
°C
7
Hot filament ignition temperature
2.0mm
IEC60695-2-13
°C
7
Hot filament ignition temperature
3.0mm
IEC60695-2-13
°C
7
Burning wire flammability index
1.0mm
IEC60695-2-12
°C
9