LCP VECTRA® A115 CELANESE USA

115

Unit Price:
$6222 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
50MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Halogen-free Flame retardant
Application Areas:Electrical tools Home appliance components Automotive Applications
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	Across Flow	ISO 294-4	0.40	%
Shrinkage rate	Shrinkage rate	流量	ISO 294-4	0.10	%
Water absorption rate	Saturation, 23°C	ISO 62	6.0E-3	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	3.0E-3	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus		ISO 527-2/1A	12000	Mpa
Tensile stress	Break	ISO 527-2/1A/5	200	Mpa
Tensile strain	Break	ISO 527-2/1A/5	3.1	%
Bending modulus	23°C	ISO 178	12400	Mpa
Bending stress	23°C	ISO 178	250	Mpa
Compressive modulus		ISO 604	10000	Mpa
Compressive stress	1% Strain	ISO 604	85.0	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	250	°C
	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	230	°C
	Hot deformation temperature	Hot deformation temperature	8.0 MPa, Unannealed	ISO 75-2/C	157	°C
Vicat softening temperature		ISO 306/B50	162	°C
Melting temperature 3		ISO 11357-3	280	°C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	1.0E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	1.8E-5	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC 60093	> 1.0E+15	ohms
Volume resistivity		IEC 60093	1.0E+15	ohms·cm
Dielectric strength		IEC 60243-1	34	KV/mm
Relative permittivity	100 Hz	IEC 60250	3.50
Relative permittivity	Relative permittivity	1 MHz	IEC 60250	3.00
Dissipation factor	100 Hz	IEC 60250	0.020
Dissipation factor	Dissipation factor	1 MHz	IEC 60250	0.018
Arc resistance		内部方法	135	sec
Leakage Trace Index		IEC 60112	200	V

injection	Test Result	Unit
drying temperature	150	°C
drying time	4.0 到 6.0	hr
Suggested maximum moisture content	0.010	%
Hopper temperature	20 到 30	°C
Temperature at the rear of the barrel	270 到 280	°C
Temperature in the middle of the barrel	275 到 285	°C
Temperature at the front of the material cylinder	280 到 290	°C
Spray nozzle temperature	290 到 300	°C
Processing (melt) temperature	285 到 295	°C
Mold temperature	80 到 120	°C
Injection speed	快速
Back pressure	< 3.00	Mpa

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	48	kJ/m²
Unscented Izod impact strength	23°C	ISO 180/1U	61	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M -Sale	ISO 2039-2	80

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating		UL 94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.