Shrinkage rate

横向流量

ISO 294-4

%

0

Shrinkage rate

流量

ISO 294-4

%

0

Water absorption rate

饱和, 23°C

ISO 62

%

6

Water absorption rate

平衡, 23°C, 50% RH

ISO 62

%

3

Tensile modulus

ISO 527-2/1A

Mpa

1

Tensile strain

断裂

ISO 527-2/1A/5

%

3

Tensile stress

断裂

ISO 527-2/1A/5

Mpa

2

Bending modulus

23°C

ISO 178

Mpa

1

Bending stress

23°C

ISO 178

Mpa

2

Compressive modulus

ISO 604

Mpa

1

Compressive stress

1% 应变

ISO 604

Mpa

8

Hot deformation temperature

0.45 MPa, 未退火

ISO 75-2/B

°C

2

Hot deformation temperature

1.8 MPa, 未退火

ISO 75-2/A

°C

2

Hot deformation temperature

8.0 MPa, 未退火

ISO 75-2/C

°C

1

Melting temperature 3

ISO 11357-3

°C

2

Vicat softening temperature

ISO 306/B50

°C

1

Linear coefficient of thermal expansion

流动

ISO 11359-2

cm/cm/°C

1

Linear coefficient of thermal expansion

横向

ISO 11359-2

cm/cm/°C

1

Surface resistivity

IEC 60093

ohms

>

Dielectric strength

IEC 60243-1

KV/mm

3

Leakage Trace Index

IEC 60112

V

2

Arc resistance

内部方法

sec

1

Volume resistivity

IEC 60093

ohms·cm

1

Impact strength of simply supported beam without notch

23°C

ISO 179/1eU

kJ/m²

4

Unscented Izod impact strength

23°C

ISO 180/1U

kJ/m²

6