PC/ABS INFINO® HM-1100 K21294 Samsung Cheil South Korea
131
- Unit Price:
- $3983 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 24MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Flame retardant Filler: Glass fiber reinf
- Application Areas:TV Electronic and Electrical
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ASTMD955 | 0.10 | % |
| TD | ASTMD955 | 0.10 | % | |
| TD | ISO2577 | 0.10 | % | |
| MD:3.20mm | ISO2577 | 0.10 | % | |
| Melt mass flow rate | 220°C/10.0kg | ASTMD1238 | 22 | g/10min |
| 250°C/2.16kg | ASTMD1238 | 7.0 | g/10min | |
| 220°C/10.0kg | ISO1133 | 22 | g/10min | |
| 250°C/2.16kg | ISO1133 | 7.0 | g/10min | |
| Ash Content | -- | ISO3451 | 9.5 | % |
| -- | ASTMD5630 | 9.5 | % | |
| Tg(halfwidth)-DSC | 101 | °C |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength 2 | Yield | ASTMD638 | 59.0 | Mpa |
| Break | ASTMD638 | 59.0 | Mpa | |
| Elongation rate 2 | Break | ASTMD638 | 4.0 | % |
| Bending strength 3 | ASTMD790 | 96.0 | Mpa | |
| Bending stress 4 | ISO178 | 95.0 | Mpa | |
| Tensile modulus 2 | ASTMD638 | 3400 | Mpa | |
| Bending modulus 4 | ISO178 | 3800 | Mpa | |
| Bending modulus 3 | ASTMD790 | 3900 | Mpa | |
| Tensile stress | Yield | ISO527-2/5 | 55.0 | Mpa |
| Break | ISO527-2/5 | 55.0 | Mpa | |
| Tensile strain | Break | ISO527-2/5 | 4.0 | % |
| Tensile modulus | ISO527-2/5 | 3400 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 97.0 | °C |
| 0.45MPa,Unannealed,4.00mm | ISO75-2/B | 97.0 | °C | |
| 0.45MPa,Annealed,4.00mm | ISO75-2/B | 102 | °C | |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 96.0 | °C | |
| 1.8MPa,Unannealed,4.00mm | ISO75-2/A | 96.0 | °C | |
| 1.8MPa,Annealed,4.00mm | ISO75-2/A | 98.0 | °C | |
| Vicat softening temperature | ISO306/B50 | 99.0 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Suspended wall beam gap impact strength 5 | 23°C | ISO180/1A | 8.0 | kJ/m² |
| CharpyNotchedImpactStrength5 | 23°C | ISO179/1eA | 7.0 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ASTMD785 | 118 | |
| R-Scale | ISO2039-2 | 118 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 2.0mm | UL94 | V-0 | |
| 3.0mm | UL94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.