Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS HM-1100 K21294 Samsung Cheil South Korea
INFINO®
TV、Electronic and Electrical
Glass fiber reinforced、Flame retardant、Filler: Glass fiber reinf
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/ABS/Samsung Cheil South Korea/HM-1100 K21294
Ash Content
--
ISO3451
%
9
Ash Content
--
ASTMD5630
%
9
Melt mass flow rate
220°C/10.0kg
ASTMD1238
g/10min
2
Melt mass flow rate
250°C/2.16kg
ASTMD1238
g/10min
7
Melt mass flow rate
220°C/10.0kg
ISO1133
g/10min
2
Melt mass flow rate
250°C/2.16kg
ISO1133
g/10min
7
Shrinkage rate
MD：3.20mm
ASTMD955
%
0
Shrinkage rate
TD
ASTMD955
%
0
Shrinkage rate
TD
ISO2577
%
0
Shrinkage rate
MD:3.20mm
ISO2577
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/ABS/Samsung Cheil South Korea/HM-1100 K21294
Tensile strength 2
屈服
ASTMD638
Mpa
5
Tensile strength 2
断裂
ASTMD638
Mpa
5
Tensile modulus
ISO527-2/5
Mpa
3
Tensile modulus 2
ASTMD638
Mpa
3
Tensile strain
断裂
ISO527-2/5
%
4
Tensile stress
断裂
ISO527-2/5
Mpa
5
Tensile stress
屈服
ISO527-2/5
Mpa
5
Elongation rate 2
断裂
ASTMD638
%
4
Bending modulus 3
ASTMD790
Mpa
3
Bending modulus 4
ISO178
Mpa
3
Bending strength 3
ASTMD790
Mpa
9
Bending stress 4
ISO178
Mpa
9
Thermal performance
Test Condition
Test Method
Unit
PC/ABS/Samsung Cheil South Korea/HM-1100 K21294
Hot deformation temperature
0.45MPa,未退火,6.40mm
ASTMD648
°C
9
Hot deformation temperature
0.45MPa,Unannealed,4.00mm
ISO75-2/B
°C
9
Hot deformation temperature
0.45MPa,Annealed,4.00mm
ISO75-2/B
°C
1
Hot deformation temperature
1.8MPa,未退火,6.40mm
ASTMD648
°C
9
Hot deformation temperature
1.8MPa,Unannealed,4.00mm
ISO75-2/A
°C
9
Hot deformation temperature
1.8MPa,Annealed,4.00mm
ISO75-2/A
°C
9
Vicat softening temperature
ISO306/B50
°C
9
Impact performance
Test Condition
Test Method
Unit
PC/ABS/Samsung Cheil South Korea/HM-1100 K21294
CharpyNotchedImpactStrength5
23°C
ISO179/1eA
kJ/m²
7
Suspended wall beam gap impact strength 5
23°C
ISO180/1A
kJ/m²
8