PC LEXAN™ XHT1141-BK1C141 SABIC INNOVATIVE US
116
- Unit Price:
- $4832 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 64MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility
- Application Areas:Architectural Application Automotive External Parts Lighting applications
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | Saturation, 23°C | ISO 62 | 0.30 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.30 | % | |
| Molten Volume Flow Rate (MVR) | 300°C/1.2 kg | ISO 1133 | 16.0 | cm3/10min |
| 330°C/2.16 kg | ISO 1133 | 70.0 | cm3/10min | |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.60 到 0.90 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending modulus 1 | ISO 178 | 2400 | Mpa | |
| Bending stress 1, 2 | ISO 178 | 100 | Mpa | |
| Tensile modulus | ISO 527-2/1 | 2400 | Mpa | |
| Tensile stress | Yield | ISO 527-2/50 | 65.0 | Mpa |
| Break | ISO 527-2/50 | 60.0 | Mpa | |
| Tensile strain | Yield | ISO 527-2/50 | 6.5 | % |
| Break | ISO 527-2/50 | 80 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ISO 11359-2 | 7.0E-5 | cm/cm/°C |
| Across Flow : -40°C | ISO 11359-2 | 7.0E-5 | cm/cm/°C | |
| Vicat softening temperature | -- | ISO 306/B50 | 150 | °C |
| -- | ISO 306/B120 | 152 | °C | |
| Hot deformation temperature 5 | 0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span | ISO 75-2/Bf | 144 | °C |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span | ISO 75-2/Af | 132 | °C |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 125 | °C | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Processing (melt) temperature | 290 到 335 | °C | ||
| Mold temperature | 85 到 130 | °C | ||
| drying time | 4.0 到 6.0 | hr | ||
| Suggested injection volume | 40 到 60 | % | ||
| Temperature at the rear of the barrel | 270 到 315 | °C | ||
| Temperature in the middle of the barrel | 280 到 325 | °C | ||
| Temperature at the front of the material cylinder | 290 到 335 | °C | ||
| Spray nozzle temperature | 285 到 330 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 40 到 90 | rpm | ||
| Exhaust hole depth | 0.025 到 0.080 | mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap 3 | -30°C | ISO 179/1eA | 12 | kJ/m² |
| 23°C | ISO 179/1eA | 16 | kJ/m² | |
| Simply supported beam without notch impact strength 3 | -30°C | ISO 179/1eU | 无断裂 | |
| 23°C | ISO 179/1eU | 无断裂 | ||
| Suspended wall beam gap impact strength 4 | -30°C | ISO 180/1A | 10 | kJ/m² |
| 23°C | ISO 180/1A | 14 | kJ/m² | |
| Unscented Izod Impact Strength 4 | -30°C | ISO 180/1U | 无断裂 | |
| 23°C | ISO 180/1U | 无断裂 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.