Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC XHT1141-BK1C141 SABIC INNOVATIVE US
LEXAN™
Architectural Application、Automotive External Parts、Lighting applications
High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/XHT1141-BK1C141
Molten Volume Flow Rate (MVR)
300°C/1.2 kg
ISO 1133
cm3/10min
1
Molten Volume Flow Rate (MVR)
330°C/2.16 kg
ISO 1133
cm3/10min
7
Shrinkage rate - flow
3.20 mm
内部方法
%
0
Water absorption rate
饱和, 23°C
ISO 62
%
0
Water absorption rate
平衡, 23°C, 50% RH
ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/XHT1141-BK1C141
Tensile modulus
ISO 527-2/1
Mpa
2
Tensile strain
屈服
ISO 527-2/50
%
6
Tensile strain
断裂
ISO 527-2/50
%
8
Tensile stress
屈服
ISO 527-2/50
Mpa
6
Tensile stress
断裂
ISO 527-2/50
Mpa
6
Bending modulus 1
ISO 178
Mpa
2
Bending stress 1, 2
ISO 178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/XHT1141-BK1C141
Hot deformation temperature 5
0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距
ISO 75-2/Bf
°C
1
Hot deformation temperature 5
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距
ISO 75-2/Af
°C
1
Vicat softening temperature
--
ISO 306/B50
°C
1
Vicat softening temperature
--
ISO 306/B120
°C
1
Linear coefficient of thermal expansion
流动 : -40 到 40°C
ISO 11359-2
cm/cm/°C
7
Linear coefficient of thermal expansion
横向 : -40°C
ISO 11359-2
cm/cm/°C
7
Impact performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/XHT1141-BK1C141
Impact strength of simply supported beam gap 3
-30°C
ISO 179/1eA
kJ/m²
1
Impact strength of simply supported beam gap 3
23°C
ISO 179/1eA
kJ/m²
1
Suspended wall beam gap impact strength 4
-30°C
ISO 180/1A
kJ/m²
1
Suspended wall beam gap impact strength 4
23°C
ISO 180/1A
kJ/m²
1