PC LEXAN™ 9330-759 SABIC INNOVATIVE NANSHA
87
- Unit Price:
- $4624 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 15MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant Toughening UV resistance
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD:3.20mm | 内部方法 | 0.40到0.80 | % |
| TD:3.20mm | 内部方法 | 0.40到0.80 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.35 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.15 | % | |
| Melt mass flow rate | 300°C/1.2kg | ASTMD1238 | 10 | g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 9.00 | cm3/10min |
| Outdoor applicability | UL746C | f1 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending stress | --6,7 | ISO178 | 85.0 | Mpa |
| Yield,50.0mmSpan5 | ASTMD790 | 88.0 | Mpa | |
| Tensile strength | Yield4 | ASTMD638 | 58.0 | Mpa |
| Yield | ISO527-2/50 | 55.0 | Mpa | |
| Break4 | ASTMD638 | 61.0 | Mpa | |
| Break | ISO527-2/50 | 60.0 | Mpa | |
| Tensile modulus | --3 | ASTMD638 | 2100 | Mpa |
| -- | ISO527-2/1 | 2100 | Mpa | |
| elongation | Break | ISO527-2/50 | 130 | % |
| Yield4 | ASTMD638 | 6.0 | % | |
| Yield | ISO527-2/50 | 6.0 | % | |
| Break4 | ASTMD638 | 130 | % | |
| Bending modulus | 50.0mmSpan5 | ASTMD790 | 2070 | Mpa |
| --6 | ISO178 | 2200 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 134 | °C |
| 0.45MPa,Unannealed,100mmSpan12 | ISO75-2/Be | 135 | °C | |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 120 | °C | |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 124 | °C | |
| 1.8MPa,Unannealed,100mmSpan12 | ISO75-2/Ae | 124 | °C | |
| RTIElec | UL746 | 125 | °C | |
| Evolution Calendar intelligent importer | UL746 | 115 | °C | |
| Vicat softening temperature | -- | ASTMD152513,ISO306/B12013 | 142 | °C |
| -- | ISO306/B50 | 140 | °C | |
| Linear coefficient of thermal expansion | MD:-40to40°C | ASTME831 | 6.7E-05 | cm/cm/°C |
| MD:23to80°C | ISO11359-2 | 7.2E-05 | cm/cm/°C | |
| TD:-40to40°C | ASTME831 | 6.7E-05 | cm/cm/°C | |
| TD:23to80°C | ISO11359-2 | 7.7E-05 | cm/cm/°C | |
| RTI | UL746 | 120 | °C | |
| BallPressure Test | 125°C | IEC60695-10-2 | 通过 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compared to the anti leakage trace index | CTI | UL746 | PLC3 | |
| Hot wire ignition | HWI | UL746 | PLC1 | |
| High arc combustion index | HAI | UL746 | PLC0 | |
| Dielectric strength | 3.20mm,inOil | ASTMD149 | 17 | KV/mm |
| 3.20mm,in Oil | IEC60243-1 | 16 | KV/mm | |
| Leakage Trace Index | IEC60112 | 225 | V | |
| Dissipation factor | 50Hz | ASTMD150 | 2.4E-03 | |
| 60Hz | ASTMD150 | 2.4E-03 | ||
| 1MHz | ASTMD150,IEC60250 | 8.5E-03 | ||
| 50Hz | IEC60250 | 1E-03 | ||
| 60Hz | IEC60250 | 1E-03 | ||
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Cantilever beam without notch impact strength | 23°C11 | 内部方法 | 1100 | J/m |
| -30°C9 | ISO180/1U | 无断裂 | ||
| 23°C9 | ISO180/1U | 无断裂 | ||
| Impact strength of simply supported beam gap 8 | -30°C | ISO179/1eA | 60 | kJ/m² |
| 23°C | ISO179/1eA | 75 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 52.0 | J |
| Simple supported beam without notch impact strength 8 | -30°C | ISO179/1eU | 无断裂 | |
| 23°C | ISO179/1eU | 无断裂 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | H358/30 | ISO2039-1 | 90.0 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot filament ignition temperature | 1.0mm | IEC60695-2-13 | 825 | °C |
| Extreme Oxygen Index | ISO4589-2 | 35 | % | |
| UL flame retardant rating | 0.8mm | UL94 | V-1 | |
| 1.5mm | UL94 | V-0 | ||
| 3.0mm | UL94 | 5VA | ||
| Burning wire flammability index | 1.0mm | IEC60695-2-12 | 960 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.