Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 9330-759 SABIC INNOVATIVE NANSHA
LEXAN™
--
Flame retardant、Toughening、UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/9330-759
Melt volume flow rate
300°C/1.2kg
ISO1133
cm3/10min
9
Melt mass flow rate
300°C/1.2kg
ASTMD1238
g/10min
1
Shrinkage rate
MD:3.20mm
内部方法
%
0
Shrinkage rate
TD:3.20mm
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/9330-759
Tensile strength
屈服4
ASTMD638
Mpa
5
Tensile strength
屈服
ISO527-2/50
Mpa
5
Tensile strength
断裂4
ASTMD638
Mpa
6
Tensile strength
断裂
ISO527-2/50
Mpa
6
Tensile modulus
--3
ASTMD638
Mpa
2
Tensile modulus
--
ISO527-2/1
Mpa
2
elongation
屈服4
ASTMD638
%
6
elongation
屈服
ISO527-2/50
%
6
elongation
断裂4
ASTMD638
%
1
elongation
断裂
ISO527-2/50
%
1
Bending modulus
50.0mm跨距5
ASTMD790
Mpa
2
Bending modulus
--6
ISO178
Mpa
2
Bending stress
--6,7
ISO178
Mpa
8
Bending stress
屈服,50.0mm跨距5
ASTMD790
Mpa
8
Thermal performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/9330-759
RTI
UL746
°C
1
RTIElec
UL746
°C
1
Evolution Calendar intelligent importer
UL746
°C
1
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
0.45MPa,未退火,100mm跨距12
ISO75-2/Be
°C
1
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,未退火,6.40mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,未退火,100mm跨距12
ISO75-2/Ae
°C
1
Vicat softening temperature
--
ASTMD152513,ISO306/B12013
°C
1
Vicat softening temperature
--
ISO306/B50
°C
1
Linear coefficient of thermal expansion
MD:-40到40°C
ASTME831
cm/cm/°C
6
Linear coefficient of thermal expansion
MD:23到80°C
ISO11359-2
cm/cm/°C
7
Linear coefficient of thermal expansion
TD:-40到40°C
ASTME831
cm/cm/°C
6
Linear coefficient of thermal expansion
TD:23到80°C
ISO11359-2
cm/cm/°C
7
Electrical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/9330-759
Surface resistivity
IEC60093
ohms
>
Dielectric strength
3.20mm,inOil
ASTMD149
KV/mm
1
Dielectric strength
3.20mm,在油中
IEC60243-1
KV/mm
1
Leakage Trace Index
IEC60112
V
2
Volume resistivity
IEC60093
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/9330-759
Impact strength of simply supported beam gap 8
-30°C
ISO179/1eA
kJ/m²
6
Impact strength of simply supported beam gap 8
23°C
ISO179/1eA
kJ/m²
7
Cantilever beam without notch impact strength
23°C11
内部方法
J/m
1
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
5
hardness
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/9330-759
Ball pressure hardness
H358/30
ISO2039-1
Mpa
9
flammability
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/9330-759
Extreme Oxygen Index
ISO4589-2
%
3
Hot filament ignition temperature
1.0mm
IEC60695-2-13
°C
8
Burning wire flammability index
1.0mm
IEC60695-2-12
°C
9