PC LEXAN™ HF1110 7B1D011 SABIC INNOVATIVE NANSHA
105
Unit Price:$3517 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility High temperature resistan transparent
- Application Areas:High mobility High temperature resistan transparent
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | 24 hr | ASTM D570 | 0.10 | % |
| Equilibrium, 23°C | ASTM D570 | 0.35 | % | |
| Equilibrium, 100°C | ASTM D570 | 0.58 | % | |
| Melt flow rate | 300°C/1.2 kg | ASTM D1238 | 25 | g/10 min |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| elongation | Break | ASTM D638 | 120 | % |
| Bending modulus | 50.0 mm Span | ASTM D790 | 2300 | Mpa |
| bending strength | Yield, 50.0 mm Span | ASTM D790 | 93.0 | Mpa |
| Tensile strength | Yield | ASTM D638 | 62.0 | Mpa |
| Break | ASTM D638 | 65.0 | Mpa | |
| Tensile impact strength | ASTM D1822 | 378 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C, Energy at Peak | ASTM D3763 | 54.0 | J |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Thermal deformation temperature under load | 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 126 | °C |
| RTI | UL 746 | 130 | °C | |
| RTI Imp | UL 746 | 130 | °C | |
| RTI Elec | UL 746 | 130 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 2 | ||
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 2 | ||
| Hot wire ignition (HWI) | UL 746 | PLC 2 | ||
| High arc combustion index (HAI) | UL 746 | PLC 1 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 120 | °C | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Processing (melt) temperature | 270 到 295 | °C | ||
| Mold temperature | 70 到 95 | °C | ||
| drying time | 3.0 到 4.0 | hr | ||
| Suggested injection volume | 40 到 60 | % | ||
| Temperature at the rear of the barrel | 250 到 270 | °C | ||
| Temperature in the middle of the barrel | 260 到 280 | °C | ||
| Temperature at the front of the material cylinder | 270 到 295 | °C | ||
| Spray nozzle temperature | 265 到 290 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 40 到 70 | rpm | ||
| Exhaust hole depth | 0.025 到 0.076 | mm |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Light transmittance | 2540 µm | ASTM D1003 | 88.0 | % |
| Haze | 2540 µm | ASTM D1003 | 1.0 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.1 mm | UL 94 | V-2 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.