Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC HF1110 7B1D011 SABIC INNOVATIVE NANSHA
LEXAN™
High mobility、High temperature resistan、transparent
High mobility、High temperature resistan、transparent
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/HF1110 7B1D011
Melt flow rate
300°C/1.2 kg
ASTM D1238
g/10 min
2
Shrinkage rate - flow
3.20 mm
内部方法
%
0
Water absorption rate
24 hr
ASTM D570
%
0
Water absorption rate
平衡, 23°C
ASTM D570
%
0
Water absorption rate
平衡, 100°C
ASTM D570
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/HF1110 7B1D011
Tensile strength
屈服
ASTM D638
Mpa
6
Tensile strength
断裂
ASTM D638
Mpa
6
Tensile impact strength
ASTM D1822
kJ/m²
3
elongation
断裂
ASTM D638
%
1
Bending modulus
50.0 mm 跨距
ASTM D790
Mpa
2
bending strength
屈服, 50.0 mm 跨距
ASTM D790
Mpa
9
Dart impact equipped with measuring instruments
23°C, Energy at Peak
ASTM D3763
J
5
Thermal performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/HF1110 7B1D011
RTI
UL 746
°C
1
RTI Elec
UL 746
°C
1
RTI Imp
UL 746
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 3.20 mm
ASTM D648
°C
1
optical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/HF1110 7B1D011
Light transmittance
2540 µm
ASTM D1003
%
8
Haze
2540 µm
ASTM D1003
%
1