PC LEXAN™ LUX2614 SABIC INNOVATIVE NANSHA

Unit Price:
$3257 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant UV resistance
Application Areas:UV resistance Flame retardant
Color:--
Grade:Light diffusion level

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Water absorption rate	24 hr	ASTM D570	0.15	%
	Water absorption rate	Equilibrium, 23°C	ASTM D570	0.35	%
	Water absorption rate	Water absorption rate	Equilibrium, 100°C	ASTM D570	0.58	%
Melt flow rate	300°C/1.2 kg	ASTM D1238	7.0	g/10 min
Molten Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	7.00	cm3/10min
Specific volume		ASTM D792	0.830	cm³/g
Outdoor applicability		UL 746C	f2
Shrinkage rate - flow	3.20 mm	内部方法	0.50 到 0.70	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Bending stress	-- 4, 5	ISO 178	94.0	Mpa
Bending stress	Bending stress	Yield, 50.0 mm Span 3	ASTM D790	93.0	Mpa
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	ASTM D1044	10.0	mg
Tensile strength	Yield 2	ASTM D638	62.0	Mpa
	Tensile strength	Yield	ISO 527-2/50	63.0	Mpa
		Tensile strength	Break 2	ASTM D638	65.0	Mpa
		Tensile strength	Tensile strength	Break	ISO 527-2/50	63.0	Mpa
Tensile modulus		ISO 527-2/1	2300	Mpa
elongation	Yield 2	ASTM D638	7.0	%
	elongation	Yield	ISO 527-2/50	6.0	%
	elongation	elongation	Break 2	ASTM D638	110	%
Bending modulus	50.0 mm Span 3	ASTM D790	2340	Mpa
Bending modulus	Bending modulus	-- 4	ISO 178	2300	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Vicat softening temperature	--	ASTM D15257	154	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	145	°C
specific heat		ASTM C351	1260	J/kg/°C
thermal conductivity		ASTM C177	0.29	W/m/K
RTI		UL 746	80.0	°C
RTI Imp		UL 746	80.0	°C
RTI Elec		UL 746	80.0	°C
Thermal deformation temperature under load	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	137	°C
Thermal deformation temperature under load	Thermal deformation temperature under load	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	132	°C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion - flow	-40 to 95°C	ASTM E831	6.8E-5	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Compared to the Leakage Tracking Index (CTI)		UL 746	PLC 3
Hot wire ignition (HWI)		UL 746	PLC 3
Dielectric strength	3.20 mm, in Air	ASTM D149	15	KV/mm
High arc combustion index (HAI) 8		UL 746	PLC 1
Dissipation factor	50 Hz	ASTM D150	9.0E-4
	Dissipation factor	60 Hz	ASTM D150	9.0E-4
	Dissipation factor	Dissipation factor	1 MHz	ASTM D150	0.010
Dielectric constant	60 Hz	ASTM D150	3.17
	Dielectric constant	50 kHz	ASTM D150	3.17
	Dielectric constant	Dielectric constant	1 MHz	ASTM D150	2.96
Volume resistivity		ASTM D257	> 1.0E+17	ohms·cm

injection	Test Result	Unit
drying time	3.0 到 4.0	hr
Suggested injection volume	40 到 60	%
Temperature at the rear of the barrel	290 到 310	°C
Temperature in the middle of the barrel	300 到 320	°C
Temperature at the front of the material cylinder	310 到 330	°C
Spray nozzle temperature	305 到 325	°C
Back pressure	0.300 到 0.700	Mpa
Screw speed	40 到 70	rpm
Exhaust hole depth	0.025 到 0.076	mm
drying temperature	120	°C
Suggested maximum moisture content	0.020	%
Processing (melt) temperature	310 到 330	°C
Mold temperature	80 到 115	°C

Impact performance	Test Condition	Test Method	Test Result	Unit
Falling hammer impact	23°C	ASTM D3029	169	J
Non notched cantilever beam impact	23°C	ASTM D4812	3200	J/m
Tensile impact strength 6		ASTM D1822	546	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M-Scale	ASTM D785	70
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	118

optical performance	Test Condition	Test Method	Test Result	Unit
Refractive index		ASTM D542	1.586

flammability	Test Condition	Test Method	Test Result	Unit
Burning wire flammability index	0.75 mm	IEC 60695-2-12	750	°C
Burning wire flammability index	Burning wire flammability index	1.5 mm	IEC 60695-2-12	850	°C
Hot filament ignition temperature	0.75 mm 9	IEC 60695-2-13	875	°C
Hot filament ignition temperature	Hot filament ignition temperature	1.5 mm	IEC 60695-2-13	850	°C
UL flame retardant rating	0.8 to 1.7 mm	UL 94	V-2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.