Melt flow rate

300°C/1.2 kg

ASTM D1238

g/10 min

7

Molten Volume Flow Rate (MVR)

300°C/1.2 kg

ISO 1133

cm3/10min

7

Shrinkage rate - flow

3.20 mm

内部方法

%

0

Specific volume

ASTM D792

cm³/g

0

Water absorption rate

24 hr

ASTM D570

%

0

Water absorption rate

平衡, 23°C

ASTM D570

%

0

Water absorption rate

平衡, 100°C

ASTM D570

%

0

Tensile strength

屈服 2

ASTM D638

Mpa

6

Tensile strength

屈服

ISO 527-2/50

Mpa

6

Tensile strength

断裂 2

ASTM D638

Mpa

6

Tensile strength

断裂

ISO 527-2/50

Mpa

6

Tensile modulus

ISO 527-2/1

Mpa

2

elongation

屈服 2

ASTM D638

%

7

elongation

屈服

ISO 527-2/50

%

6

elongation

断裂 2

ASTM D638

%

1

Taber abraser

1000 Cycles, 1000 g, CS-17 转轮

ASTM D1044

mg

1

Bending modulus

50.0 mm 跨距 3

ASTM D790

Mpa

2

Bending modulus

-- 4

ISO 178

Mpa

2

Bending stress

-- 4, 5

ISO 178

Mpa

9

Bending stress

屈服, 50.0 mm 跨距 3

ASTM D790

Mpa

9

RTI

UL 746

°C

8

RTI Elec

UL 746

°C

8

RTI Imp

UL 746

°C

8

specific heat

ASTM C351

J/kg/°C

1

thermal conductivity

ASTM C177

W/m/K

0

Vicat softening temperature

--

ASTM D15257

°C

1

Vicat softening temperature

--

ISO 306/B120

°C

1

Linear coefficient of thermal expansion - flow

-40 到 95°C

ASTM E831

cm/cm/°C

6

Thermal deformation temperature under load

0.45 MPa, 未退火, 6.40 mm

ASTM D648

°C

1

Thermal deformation temperature under load

1.8 MPa, 未退火, 6.40 mm

ASTM D648

°C

1

Dielectric strength

3.20 mm, in Air

ASTM D149

KV/mm

1

Volume resistivity

ASTM D257

ohms·cm

>

Tensile impact strength 6

ASTM D1822

kJ/m²

5

Falling hammer impact

23°C

ASTM D3029

J

1

Non notched cantilever beam impact

23°C

ASTM D4812

J/m

3

Hot filament ignition temperature

0.75 mm 9

IEC 60695-2-13

°C

8

Hot filament ignition temperature

1.5 mm

IEC 60695-2-13

°C

8

Burning wire flammability index

0.75 mm

IEC 60695-2-12

°C

7

Burning wire flammability index

1.5 mm

IEC 60695-2-12

°C

8