PC PANLITE® ML-5206ZHP TEIJIN JAPAN
125
Unit Price:$4958 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 34MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability transparent
- Application Areas:Fitness equipment Casters
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 2.50 | cm3/10min |
| Shrinkage rate | TD:4.00mm | 内部方法 | 0.50到0.70 | % |
| MD:4.00mm | 内部方法 | 0.50到0.70 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.20 | % |
| Dissolving fingers | 300℃ | ISO 1133 | 2.5 | cm310min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Yield tensile strength | 50mm/min | ISO 527-1,2 | 65 | Mpa |
| Tensile strength at break | 50mm/min | ISO 527-1 | 53 | Mpa |
| Tensile modulus | ISO527-2/1 | 2400 | Mpa | |
| Tensile stress | Yield | ISO527-2/50 | 65.0 | Mpa |
| Break | ISO527-2/50 | 53.0 | Mpa | |
| Tensile strain | Yield | ISO527-2/50 | 6.0 | % |
| Nominal tensile fracture strain | ISO527-2/50 | 25 | % | |
| Bending modulus 3 | ISO178 | 2350 | Mpa | |
| Bending stress 3 | ISO178 | 97.0 | Mpa | |
| elongation at break | 50mm/min | ISO 527-1 | 25 | % |
| Bending modulus | 2mm/min | ISO 178 | 2350 | Mpa |
| bending strength | 2mm/min | ISO 178 | 97 | Mpa |
| Gap impact strength | Notched | ISO 179 | 9.0 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.80MPa | ISO 75-1,2 | 123 | °C |
| 阻燃性，1.5mm(3.2mm) | UL94 | V-0(5VA) | ||
| 1.8MPa,Unannealed | ISO75-2/A | 123 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 7E-05 | cm/cm/°C |
| TD | ISO11359-2 | 7E-05 | cm/cm/°C | |
| RTIElec | 1.5mm | UL746 | 130 | °C |
| Evolution Calendar intelligent importer | 1.5mm | UL746 | 125 | °C |
| RTI | 1.5mm | UL746 | 130 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 无断裂 |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| transmissivity | 3000µm | ASTMD1003 | 77.0 | % |
| Light transmittance | 1.5mmt | JIS K7136 | 85 | % |
| Dispersion degree | 2.0mmt | In-house method | 17 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | V-0 | |
| 3.2mm | UL94 | 5VA | ||
| Burning wire flammability index | 1.5mm | IEC60695-2-12 | 960 | °C |
| 3.0mm | IEC60695-2-12 | 960 | °C | |
| Hot filament ignition temperature | 1.5mm | IEC60695-2-13 | 850 | °C |
| 3.0mm | IEC60695-2-13 | 850 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.