PC IUPILON™ EFR3000 BK MITSUBISHI ENGINEERING JAPAN

229

Unit Price:
$3304 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
36.1MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High mobility Flame retardant
Application Areas:Non specific food
Color:--
Grade:Injection grade

Technical Data Sheet Compare

Physical properties	Test Method	Test Result	Unit
density	ASTM D792/ISO 1183	1.19
Molding shrinkage rate	ASTM D955	0.5 - 0.7	%
Water absorption rate 23 ℃/24h	ASTM D570/ISO 62	0.24	%

physical property	Test Condition	Test Method	Test Result	Unit
Melt mass flow rate	300°C/1.2kg	ISO1133	22	g/10min
Melt volume flow rate	300°C/1.2kg	ISO1133	21.0	cm3/10min
Shrinkage rate	TD:3.20mm		0.50to0.70	%
	Shrinkage rate	MD:3.20mm		0.50to0.70	%
	Shrinkage rate	Shrinkage rate	吸水率(Saturation,23°C)		0.24	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus		ISO527-2	2300	Mpa
Tensile stress	Yield	ISO527-2	61.0	Mpa
Tensile strain	Yield	ISO527-2	4.7	%
Nominal tensile fracture strain		ISO527-2	67	%
Bending modulus		ISO178	2500	Mpa
Bending stress		ISO178	92.0	Mpa
Tensile modulus		ASTM D638/ISO 527	2300	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	2500	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	92	kg/cm²(MPa)[Lb/in²]
Tensile elongation at break (elongation at break)		ASTM D638/ISO 527	67	%

Thermal performance	Test Condition	Test Method	Test Result	Unit
Combustibility (rate)		UL94	V-0 (1.0mm)
Linear expansion coefficient		ASTM D696/ISO 11359	6.6E-05	mm/mm.℃
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	137	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	125	°C
Linear coefficient of thermal expansion	MD	ISO11359-2	6.6E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO11359-2	6.7E-05	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC60093	6E+15	ohms
Volume resistivity		IEC60093	3E+16	ohms·cm
Dielectric strength	1.00mm	IEC60243-1	31	KV/mm
Dielectric strength	Dielectric strength	3.00mm	IEC60243-1	18	KV/mm
Relative permittivity	100Hz	IEC60250	3.10
Relative permittivity	Relative permittivity	1MHz	IEC60250	3.10
Dissipation factor	100Hz	IEC60250	6E-04
Dissipation factor	Dissipation factor	1MHz	IEC60250	9E-03
Surface resistivity		ASTM D257/IEC 60093	6.E+15	Ω
Dielectric constant		ASTM D150/IEC 60250	3.1
Volume resistivity		ASTM D257/IEC 60093	3.E+14	Ω.cm

Processing performance	Test Condition	Test Method	Test Result	Unit
Dry conditions			热风干燥 120℃---約4-8小时
Processing temperature			250-280	°C
	Processing temperature			270-300	°C
	Processing temperature	Processing temperature			260-290	°C
Screw speed			50-100	rpm
Mold temperature			70-100	°C

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	23°C	ISO179	NoBreak

flammability	Test Condition	Test Method	Test Result	Unit
FlameRating	1.0mm	UL94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.