Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC EFR3000 BK MITSUBISHI ENGINEERING JAPAN
IUPILON™
Non specific food
High mobility、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
PC/MITSUBISHI ENGINEERING JAPAN/EFR3000 BK
Molding shrinkage rate
ASTM D955
%
0
Water absorption rate 23 ℃/24h
ASTM D570/ISO 62
%
0
physical property
Test Condition
Test Method
Unit
PC/MITSUBISHI ENGINEERING JAPAN/EFR3000 BK
Melt volume flow rate
300°C/1.2kg
ISO1133
cm3/10min
2
Melt mass flow rate
300°C/1.2kg
ISO1133
g/10min
2
Mechanical performance
Test Condition
Test Method
Unit
PC/MITSUBISHI ENGINEERING JAPAN/EFR3000 BK
Nominal tensile fracture strain
ISO527-2
%
6
Tensile modulus
ISO527-2
Mpa
2
Tensile modulus
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
2
Tensile strain
屈服
ISO527-2
%
4
Tensile stress
屈服
ISO527-2
Mpa
6
Bending modulus
ISO178
Mpa
2
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
2
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
9
Bending stress
ISO178
Mpa
9
Tensile elongation at break (elongation at break)
ASTM D638/ISO 527
%
6
Thermal performance
Test Condition
Test Method
Unit
PC/MITSUBISHI ENGINEERING JAPAN/EFR3000 BK
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
1
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
1
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
6
Linear coefficient of thermal expansion
TD
ISO11359-2
cm/cm/°C
6
Linear expansion coefficient
ASTM D696/ISO 11359
mm/mm.℃
6
Electrical performance
Test Condition
Test Method
Unit
PC/MITSUBISHI ENGINEERING JAPAN/EFR3000 BK
Surface resistivity
ASTM D257/IEC 60093
Ω
6
Surface resistivity
IEC60093
ohms
6
Dielectric strength
1.00mm
IEC60243-1
KV/mm
3
Dielectric strength
3.00mm
IEC60243-1
KV/mm
1
Volume resistivity
IEC60093
ohms·cm
3
Volume resistivity
ASTM D257/IEC 60093
Ω.cm
3