PC LEXAN™ 915AU SABIC INNOVATIVE NANSHA
97
- Unit Price:
- $2685 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 56MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability High temperature resistan
- Application Areas:Electrical applications Lighting applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 300°C/1.2kg | ASTMD1238 | 23 | g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 21.0 | cm3/10min |
| Shrinkage rate | MD：--1 | 内部方法 | 0.50到0.70 | % |
| MD：3.20mm | 内部方法 | 0.50到0.70 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.35 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.15 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| --2 | ASTMD638 | 2400 | Mpa | |
| Surrender 3 | ASTMD638 | 66.0 | Mpa | |
| Yield, 50.0mm span of 10 | ASTMD790 | 95.0 | Mpa | |
| yield | ISO527-2/50 | 66.0 | Mpa | |
| Fracture 4 | ASTMD638 | 66.0 | Mpa | |
| crack | ISO527-2/50 | 66.0 | Mpa | |
| Surrender 5 | ASTMD638 | 6.0 | % | |
| yield | ISO527-2/50 | 6.0 | % | |
| Fracture 6 | ASTMD638 | 100 | % | |
| crack | ISO527-2/50 | 100 | % | |
| 50.0mm span 7 | ASTMD790 | 2400 | Mpa | |
| --8 | ISO178 | 2400 | Mpa | |
| --9 | ISO178 | 98.0 | Mpa | |
| Tensile modulus | --2 | ASTMD638 | 2400 | Mpa |
| -- | ISO527-2/1 | 2400 | Mpa | |
| Tensile strength | Yield3 | ASTMD638 | 66.0 | Mpa |
| Yield | ISO527-2/50 | 66.0 | Mpa | |
| Break3 | ASTMD638 | 66.0 | Mpa | |
| Break | ISO527-2/50 | 66.0 | Mpa | |
| elongation | Yield3 | ASTMD638 | 6.0 | % |
| Yield | ISO527-2/50 | 6.0 | % | |
| Break3 | ASTMD638 | 100 | % | |
| Break | ISO527-2/50 | 100 | % | |
| Bending modulus | 50.0mmSpan4 | ASTMD790 | 2400 | Mpa |
| --5 | ISO178 | 2400 | Mpa | |
| Bending stress | --5,6 | ISO178 | 98.0 | Mpa |
| Yield,50.0mmSpan4 | ASTMD790 | 95.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flow: -40 to 40 ° C | ASTME831 | 7E-05 | cm/cm/°C | |
| Horizontal: -40 to 40 ° C | ASTME831,ISO11359-2 | 7E-05 | cm/cm/°C | |
| 0.45MPa, unannealed, 100mm span 17 | ISO75-2/Be | 134 | °C | |
| 1.8MPa, unannealed, 3.20mm | ASTMD648 | 125 | °C | |
| 1.8MPa, unannealed, 100mm span 18 | ISO75-2/Ae | 123 | °C | |
| -- | ASTMD1525,ISO306/B501219 | 140 | °C | |
| ISO306/B120 | 141 | °C | ||
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 125 | °C |
| 1.8MPa,Unannealed,100mmSpan9 | ISO75-2/Ae | 123 | °C | |
| Vicat softening temperature | -- | ASTMD152510,ISO306/B5010 | 140 | °C |
| -- | ISO306/B120 | 141 | °C | |
| Linear coefficient of thermal expansion | MD:-40to40°C | ASTME831 | 7E-05 | cm/cm/°C |
| TD:-40to40°C | ASTME831,ISO11359-2 | 7E-05 | cm/cm/°C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| -30°C11 | ISO179/1eA | 12 | kJ/m² | |
| 23°C12 | ISO179/1eA | 65 | kJ/m² | |
| 23°C | ISO179/2C | 11 | kJ/m² | |
| The impact strength of a simply supported beam without a notch is 13 | -30°C | ISO179/1eU | 无断裂 | |
| 23°C | ISO179/1eU | 无断裂 | ||
| -30°C | ASTMD256 | 110 | J/m | |
| 23°C | ASTMD256 | 650 | J/m | |
| -30°C14 | ISO180/1A | 11 | kJ/m² | |
| 23°C15 | ISO180/1A | 65 | kJ/m² | |
| Unscented Izod Impact Strength 16 | -30°C | ISO180/1U | 无断裂 | |
| 23°C | ISO180/1U | 无断裂 | ||
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 60.0 | J |
| Impact strength of simply supported beam gap 7 | 23°C | ISO179/1eA | 65 | kJ/m² |
| The impact strength of a simply supported beam without a notch is 7 | -30°C | ISO179/1eU | 无断裂 | |
| 23°C | ISO179/1eU | 无断裂 | ||
| Unscented Izod Impact Strength 8 | -30°C | ISO180/1U | 无断裂 | |
| 23°C | ISO180/1U | 无断裂 | ||
| Impact strength of simply supported beam gap 7 | -30°C | ISO179/1eA | 12 | kJ/m² |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Refractive index | ISO489 | 1.586 | ||
| transmissivity | 2540µm | ASTMD1003 | 88.0 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | V-2 | |
| 3.0mm | UL94 | V-0 | ||
| 1.50mm | UL94 | V-2 | ||
| 3.00mm | UL94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.