Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 915AU SABIC INNOVATIVE NANSHA
LEXAN™ 
Electrical applications、Lighting applications
Thermal stability、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

physical property
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/915AU
Melt volume flow rate
300°C/1.2kg
ISO1133
cm3/10min
2
Melt mass flow rate
300°C/1.2kg
ASTMD1238
g/10min
2
Shrinkage rate
MD:--1
内部方法
%
0
Shrinkage rate
MD:3.20mm
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/915AU
--
ISO527-2/1
Mpa
2
--2
ASTMD638
Mpa
2
50.0mm span 7
ASTMD790
Mpa
2
--8
ISO178
Mpa
2
--9
ISO178
Mpa
9
crack
ISO527-2/50
Mpa
6
crack
ISO527-2/50
%
1
Fracture 4
ASTMD638
Mpa
6
Fracture 6
ASTMD638
%
1
Tensile strength
屈服3
ASTMD638
Mpa
6
Tensile strength
屈服
ISO527-2/50
Mpa
6
Tensile strength
断裂3
ASTMD638
Mpa
6
Tensile strength
断裂
ISO527-2/50
Mpa
6
Tensile modulus
--2
ASTMD638
Mpa
2
Tensile modulus
--
ISO527-2/1
Mpa
2
yield
ISO527-2/50
%
6
yield
ISO527-2/50
Mpa
6
Yield, 50.0mm span of 10
ASTMD790
Mpa
9
Surrender 3
ASTMD638
Mpa
6
Surrender 5
ASTMD638
%
6
elongation
屈服3
ASTMD638
%
6
elongation
屈服
ISO527-2/50
%
6
elongation
断裂3
ASTMD638
%
1
elongation
断裂
ISO527-2/50
%
1
Bending modulus
50.0mm跨距4
ASTMD790
Mpa
2
Bending modulus
--5
ISO178
Mpa
2
Bending stress
--5,6
ISO178
Mpa
9
Bending stress
屈服,50.0mm跨距4
ASTMD790
Mpa
9
Thermal performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/915AU
--
ASTMD1525,ISO306/B501219
°C
1
--
ISO306/B120
°C
1
0.45MPa, unannealed, 100mm span 17
ISO75-2/Be
°C
1
1.8MPa, unannealed, 100mm span 18
ISO75-2/Ae
°C
1
1.8MPa, unannealed, 3.20mm
ASTMD648
°C
1
Horizontal: -40 to 40 ° C
ASTME831,ISO11359-2
cm/cm/°C
7
Flow: -40 to 40 ° C
ASTME831
cm/cm/°C
7
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,未退火,100mm跨距9
ISO75-2/Ae
°C
1
Vicat softening temperature
--
ASTMD152510,ISO306/B5010
°C
1
Vicat softening temperature
--
ISO306/B120
°C
1
Linear coefficient of thermal expansion
MD:-40到40°C
ASTME831
cm/cm/°C
7
Linear coefficient of thermal expansion
TD:-40到40°C
ASTME831,ISO11359-2
cm/cm/°C
7
Impact performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/915AU
23°C
ISO179/2C
kJ/m²
1
23°C
ASTMD256
J/m
6
23°C12
ISO179/1eA
kJ/m²
6
23°C15
ISO180/1A
kJ/m²
6
-30°C
ASTMD256
J/m
1
-30°C11
ISO179/1eA
kJ/m²
1
-30°C14
ISO180/1A
kJ/m²
1
Impact strength of simply supported beam gap 7
23°C
ISO179/1eA
kJ/m²
6
Impact strength of simply supported beam gap 7
-30°C
ISO179/1eA
kJ/m²
1
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
6
optical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/915AU
transmissivity
2540µm
ASTMD1003
%
8