PC PANLITE® L-1250Z TEIJIN SINGAPORE
105
- Unit Price:
- $2561 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan Low temperature resistanc heat-resisting transparent
- Application Areas:Electrical field Electronic field Nursing supplies Disposable tableware Medical supplies
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ISO 1183 | 1.20 | g/cm³ | |
| Molten Volume Flow Rate (MVR) | 300°C/1.2 kg | ISO 1133 | 8.00 | cm3/10min |
| Shrinkage rate | Across Flow : 4.00 mm | 内部方法 | 0.50 到 0.70 | % |
| 流量 : 4.00 mm | 内部方法 | 0.50 到 0.70 | % | |
| Water absorption rate | 24 hr, 23°C | ISO 62 | 0.20 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2400 | Mpa | |
| Tensile stress | Yield | ISO 527-2/50 | 61.0 | Mpa |
| Tensile strain | Yield | ISO 527-2/50 | 6.0 | % |
| Nominal tensile fracture strain | ISO 527-2/50 | > 50 | % | |
| Bending modulus 3 | ISO 178 | 2350 | Mpa | |
| Bending stress 3 | ISO 178 | 93.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 142 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/A | 129 | °C | |
| Vicat softening temperature | ISO 306/B50 | 149 | °C | |
| Linear coefficient of thermal expansion | Flow | ISO 11359-2 | 7.0E-5 | cm/cm/°C |
| Across Flow | ISO 11359-2 | 7.0E-5 | cm/cm/°C | |
| RTI Elec | 0.75 mm | UL 746 | 125 | °C |
| RTI Imp | 0.75 mm | UL 746 | 115 | °C |
| RTI | 0.75 mm | UL 746 | 125 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC 60093 | > 1.0E+15 | ohms | |
| Volume resistivity | IEC 60093 | > 1.0E+15 | ohms·cm | |
| Dielectric strength 4 | IEC 60243-1 | 30 | KV/mm | |
| Relative permittivity | 100 Hz | IEC 60250 | 3.10 | |
| 1 MHz | IEC 60250 | 3.00 | ||
| Dissipation factor | 100 Hz | IEC 60250 | 1.0E-3 | |
| 1 MHz | IEC 60250 | 9.0E-3 | ||
| Leakage Trace Index | IEC 60112 | 250 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | 76 | kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179 | 无断裂 |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Refractive index | ASTM D542 | 1.585 | ||
| transmissivity | 3000 µm | ASTM D1003 | 88.0 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB | |
| 0.40 mm | UL 94 | V-2 | ||
| Burning wire flammability index | 1.5 mm | IEC 60695-2-12 | 825 | °C |
| 3.0 mm | IEC 60695-2-12 | 875 | °C | |
| Hot filament ignition temperature | 1.5 mm | IEC 60695-2-13 | 850 | °C |
| 3.0 mm | IEC 60695-2-13 | 850 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.