Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC L-1250Z TEIJIN SINGAPORE
PANLITE®
Electrical field、Electronic field、Nursing supplies、Disposable tableware、Medical supplies
High temperature resistan、Low temperature resistanc、heat-resisting、transparent
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/TEIJIN SINGAPORE/L-1250Z
density
ISO 1183
g/cm³
1
Molten Volume Flow Rate (MVR)
300°C/1.2 kg
ISO 1133
cm3/10min
8
Shrinkage rate
流量 : 4.00 mm
内部方法
%
0
Shrinkage rate
横向流量 : 4.00 mm
内部方法
%
0
Water absorption rate
24 hr, 23°C
ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/TEIJIN SINGAPORE/L-1250Z
Nominal tensile fracture strain
ISO 527-2/50
%
>
Tensile modulus
ISO 527-2/1
Mpa
2
Tensile strain
屈服
ISO 527-2/50
%
6
Tensile stress
屈服
ISO 527-2/50
Mpa
6
Bending modulus 3
ISO 178
Mpa
2
Bending stress 3
ISO 178
Mpa
9
Thermal performance
Test Condition
Test Method
Unit
PC/TEIJIN SINGAPORE/L-1250Z
RTI
0.75 mm
UL 746
°C
1
RTI Elec
0.75 mm
UL 746
°C
1
RTI Imp
0.75 mm
UL 746
°C
1
Hot deformation temperature
1.8 MPa, 未退火
ISO 75-2/A
°C
1
Hot deformation temperature
0.45 MPa, 未退火
ISO 75-2/B
°C
1
Vicat softening temperature
ISO 306/B50
°C
1
Linear coefficient of thermal expansion
横向
ISO 11359-2
cm/cm/°C
7
Linear coefficient of thermal expansion
流动
ISO 11359-2
cm/cm/°C
7
Electrical performance
Test Condition
Test Method
Unit
PC/TEIJIN SINGAPORE/L-1250Z
Surface resistivity
IEC 60093
ohms
>
Dielectric strength 4
IEC 60243-1
KV/mm
3
Leakage Trace Index
IEC 60112
V
2
Volume resistivity
IEC 60093
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PC/TEIJIN SINGAPORE/L-1250Z
Charpy Notched Impact Strength
ISO 179
kJ/m²
7
flammability
Test Condition
Test Method
Unit
PC/TEIJIN SINGAPORE/L-1250Z
Hot filament ignition temperature
1.5 mm
IEC 60695-2-13
°C
8
Hot filament ignition temperature
3.0 mm
IEC 60695-2-13
°C
8
Burning wire flammability index
1.5 mm
IEC 60695-2-12
°C
8
Burning wire flammability index
3.0 mm
IEC 60695-2-12
°C
8
optical performance
Test Condition
Test Method
Unit
PC/TEIJIN SINGAPORE/L-1250Z
transmissivity
3000 µm
ASTM D1003
%
8